Effect of prior crack growth on cleavage fracture of low toughness precracked Charpy specimens

M. Scibetta

Journal of Nuclear Materials· Volume 406· Issue 1
Publisher page

Abstract

Abstract Cleavage fracture of reactor pressure vessel steels in the upper ductile to brittle transition region generally occurs with prior significant ductile crack growth. For low upper shelf materials and using PreCracked Charpy v-notch (PCCv) specimens that can be obtained from conventional surveillance programs, the effect of prior crack growth could be particularly important. In practice, the shape of the Master Curve and the failure distribution could be affected by ductile crack growth. To quantify the effect in practical applications, the effect of prior ductile on cleavage is evaluated on PCCv specimen. The methodology use finite element calculations to grow a ductile crack and infer the brittle failure probability using the local approach to fracture. It is found that for very low upper shelf toughness materials, ductile crack growth enhances the failure probability, induces a steeper failure distribution and affects the shape of the Master Curve. However, for low toughness materials, the enhanced failure probability due to crack growth is compensated by loss of constraint.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Fatigue and fracture mechanics · Metal Forming Simulation Techniques · High Temperature Alloys and Creep

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (30)

Show source-provided references
1. Lucon · Int. J. Press. Vessels Pip. · 2007 · 84 · 53610.1016/j.ijpvp.2007.05.001 ↗
2. ASTM Standard E1253, Standard Guide for Reconstitution of Irradiated Charpy-sized Specimens, ASTM International, West Conshohocken, PA, 2007, Available from: .
3. ASTM Standard E1921, Standard Test Method for Determination of Reference Temperature, To, for Ferritic Steels in the Transition Range, ASTM International, West Conshohocken, PA, 2008, Available from: .
4. Tanguy · Eng. Fract. Mech. · 2005 · 72 · 41310.1016/j.engfracmech.2004.03.011 ↗
5. Ruggieri · Int. J. Fract. · 1996 · 79 · 30910.1007/BF00018594 ↗
6. Tvergaard · Acta Metall. · 1984 · 32 · 15710.1016/0001-6160(84)90213-X ↗
7. Rousselier · Nucl. Eng. Des. · 1987 · 105 · 9710.1016/0029-5493(87)90234-2 ↗
8. Gullerud · Eng. Fract. Mech. · 2000 · 66 · 6510.1016/S0013-7944(99)00147-2 ↗
9. Mediavilla · Eng. Fract. Mech. · 2006 · 73 · 89510.1016/j.engfracmech.2005.10.011 ↗
10. Beremin · Metall. Trans. A · 1983 · 14A · 227710.1007/BF02663302 ↗
11. Esposito · Eng. Fract. Mech. · 2007 · 74 · 54910.1016/j.engfracmech.2006.07.002 ↗
12. S. Carassou, Cleavage Onset in a Low Alloy Steel: Influence of Ductile Damaged Zones around Inclusions, PhD Thesis, Ecole nationale supérieure des mines de Paris, France, 1999, pp. 1–255 (in French).
13. Bonora · Eng. Fract. Mech. · 1997 · 58 · 1110.1016/S0013-7944(97)00074-X ↗
14. Petti · Int. J. Solids Struct. · 2005 · 42 · 365510.1016/j.ijsolstr.2004.11.015 ↗
15. ASTM Standard E1820, Standard Test Method for Measurement of Fracture Toughness, ASTM International, West Conshohocken, PA, 2008, Available from: .
16. Bordet · Eng. Fract. Mech. · 2005 · 72 · 43510.1016/j.engfracmech.2004.02.009 ↗
17. Margolin · Eng. Fract. Mech. · 2008 · 75 · 348310.1016/j.engfracmech.2007.05.002 ↗
18. T.L. Anderson, R.H. Dodds Jr., Simple constraint corrections for subsize fracture toughness specimens, in: W.R. Corwin, F.M. Haggag, W.L. Server (Eds.), Small Specimen Test Techniques Applied to Nuclear Reactor Vessel Thermal Annealing and Plant Life Extension, ASTM International, West Conshohocken, PA, ASTM STP 1204, 1983, pp. 93–105.10.1520/STP12723S ↗
19. Wallin · Eng. Fract. Mech. · 2008 · 75 · 336710.1016/j.engfracmech.2007.07.018 ↗
20. Scibetta · J. ASTM Int. · 2008 · 5 · 1
21. Petti · Eng. Fract. Mech. · 2005 · 72 · 9110.1016/j.engfracmech.2004.03.009 ↗
22. Ruggieri · Eng. Fract. Mech. · 2000 · 67 · 10110.1016/S0013-7944(00)00052-7 ↗
23. M. Scibetta, Contribution to the Evaluation of the Circumferentially-Cracked Round Bar for Fracture Toughness Determination of Reactor Pressure Vessel Steels, Dissertation for the Degree of Doctor in Applied Sciences, Université de Liège, Belgium, March 1999.
24. ESI Group, SYSTUS+ 2.0, Analysis Reference Manual, 1998.
25. C. Poussard, ESIS TC8 – Numerical Round Robin on Micro Mechanical Models: Results of Phase III for the Simulation of the Brittle to Ductile transition Curve, Report CEA, DMN/SEMI/LCMI/NT/2003-035/A, 2004, pp. 1–78.
26. Scibetta · Eng. Fract. Mech. · 2006 · 73 · 52410.1016/j.engfracmech.2005.08.009 ↗
27. Standard Test Method for Fracture Toughness within Ductile-Brittle Transition Range, Standard of the 129th Committee, Japan Society for the Promotion of Science, 1995 (in Japanese).
28. E. Lucon, M. Scibetta, Assessment of the Master Curve Approach on Three Reactor Pressure Vessel Steels (JRQ, JSPS, 22NiMoCr37), Open Report SCK•CEN-BLG-869, SCK•CEN, Mol, Belgium, 2001.
29. Anderson · J. Test. Eval. · 1991 · 2 · 12310.1520/JTE12544J ↗
30. M. Nevalainen, R.H. Dodds Jr., Numerical Investigation of 3-D Constraint Effects on Brittle Fracture in SE(B) and C(T) Specimens, Report UILU-ENG-95-2001, Department of Civil Engineering, University of Illinois at Urbana – Champaign Urbana, Illinois, February 1995.