Corrosion susceptibility and chromium loss in Austenitic steels and Nickel-based alloys in molten FLiNaK at 700 °C

A comparative study was conducted to evaluate the corrosion susceptibility of 316L, 316H, Ni 200, Inconel 625, and Hastelloy N in molten FLiNaK at 700°C for 100 hours. Top-view and cross-sectional scanning electron microscopy (SEM) imaging, combined with energy-dispersive X-ray spectroscopy (EDS) mapping, were performed to investigate microstructural and compositional changes. SEM images were further processed by introducing a contrast threshold to map cavity distribution. Using EDS mapping, intergranular and intragranular Cr loss were separately characterized. The ranking of mass loss after corrosion, from highest to lowest, is as follows: 316H > 316L > Inconel 625 > Hastelloy N > Ni 200. Cr loss was found to be correlated with Mo concentration, in agreement with many previous studies, with higher Mo content resulting in reduced Cr loss. On the other hand, there is no evidence that the high carbon content in 316H enhances corrosion resistance. The relatively low solubility of carbon in austenite at the testing temperature limits the amount of dissolved carbon, therefore the carbon-retarded vacancy diffusion, and consequently the reduced Cr diffusion, were not observed.