In situ self-ion (Fe+) irradiation of ODS-FeCrAl alloy fuel cladding materials with different Cr contents: The early stages of Cr-rich α’ phase precipitation

Oxide-dispersion-strengthened FeCrAl (ODS-FeCrAl) alloys are candidate accident-tolerant fuel cladding materials for light water reactors because they demonstrate satisfactory resistance to materials degradation effects such as high-temperature oxidation, radiation-induced swelling, and creep. Their perspective deployment to market is challenged, however, by their inherent susceptibility to irradiation embrittlement caused by the precipitation of the brittle Cr-rich α’ phase at relatively low temperatures (≤475 °C). This work used in situ self-ion irradiation (150 keV Fe + ) in a transmission electron microscope to elucidate the early stages of Cr-rich α’ phase precipitation in three candidate ODS-FeCrAl alloy fuel cladding materials with different Cr contents (10, 12, and 20 wt.%) and microstructures. The early stages of the process resulting in the precipitation of the Cr-rich α’ phase in these three ODS-FeCrAl alloys under Fe + irradiation were investigated at room temperature and 300 °C up to total fluences of 1.7 × 10 15 ions·cm -2 (2 dpa) and 3.4 × 10 15 ions·cm -2 (4 dpa), using three damage dose rates (5 × 10 –5 , 3.3 × 10 –4 , and 2 × 10 –3 dpa·s -1 ). Post-irradiation examination via scanning transmission electron microscopy, energy-dispersive X-ray spectroscopy and electron energy loss spectroscopy suggested that the precipitation of the Cr-rich α’ phase might be promoted by the phase separation of the alloy matrix into Cr-rich and Fe-rich regions. Interestingly, oxygen impurities segregated preferentially in the Cr-rich regions, possibly promoting the radiation-assisted formation of the Cr-rich α’ phase. α’ phase precipitation was more pronounced at room temperature when compared to 300 °C, and it was clearly promoted by the progressive increase in the Cr content of the ODS-FeCrAl alloy.