A vacancy dynamic evolution model based on rate theory and its influence on hydrogen isotope retention behavior

Fei Sun, Xiangming Lin, Yijin Huang, Jipeng Zhu, Long Cheng, Yifan Zhang, Hai-Shan Zhou, Lai-Ma Luo, Yasuhisa Oya, Yucheng Wu

Publisher page

Abstract

In fusion environments, plasma-facing materials are subjected to the bombardment by high-energy neutrons and large fluxes plasmas, resulting in the formation of numerous irradiation defects. These defects act as trapping sites for fuel hydrogen isotopes, increasing the tritium retention. Under thermal loads at high temperatures, these defects undergo dynamic changes, leading to complex effects on hydrogen isotope transport behaviors. Understanding the evolution of defects at different temperatures and elucidating their impact on hydrogen isotope retention is essential. In this work, a dynamic evolution model of typical vacancy defects and their clusters was constructed based on rate theory and integrated into the hydrogen isotope transport model. The simulation results were compared with experimental data, showing a good agreement between the two. Further results indicated that increasing the annealing temperature reduces defect concentrations. At high temperatures, large vacancy clusters dissociate into smaller ones, with some smaller clusters annihilating and others associating to form larger clusters. In addition, the processes of vacancy clusters association and dissociation dominate this evolution. Regarding hydrogen isotope retention, defect evolution affects the concentration of deuterium (D) atoms within the material. After D is introduced into tungsten, the concentration of D corresponds to the concentration of vacancy clusters. It is found that during thermal desorption, the desorption peak corresponding to the largest vacancy clusters is more pronounced, while other clusters show less significant peaks. This is because some of the D atoms de-trapped from the vacancy clusters are released to the material surface, while others are re-trapped by larger vacancy clusters. The findings of this work will contribute to a more accurate assessment of hydrogen isotope retention under defect dynamic evolution in future fusion reactors.
Source: expertdata · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Nuclear Materials and Properties · Fusion materials and technologies · Nuclear Physics and Applications

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (47)

Show source-provided references
1. First plasma exposure of a pre-damaged ITER-like plasma-facing unit in the WEST tokamak: procedure for the PFU preparation and lessons learned10.1088/1741-4326/ac412e ↗
2. Plasma–surface interaction, scrape-off layer and divertor physics: implications for ITER10.1088/0029-5515/47/9/016 ↗
3. Enhancement of deuterium retention in damaged tungsten by plasma-induced defect clustering10.1088/1741-4326/aa856c ↗
4. Thermal desorption behavior of deuterium for 6 MeV Fe ion irradiated W with various damage concentrations10.1016/j.jnucmat.2015.03.032 ↗
5. The influence of plasma-surface interaction on the performance of tungsten at the ITER divertor vertical targets10.1088/1361-6587/aaaf62 ↗
6. Behavior of tungsten under irradiation and plasma interaction10.1016/j.jnucmat.2019.03.035 ↗
7. A review of modelling and simulation of hydrogen behaviour in tungsten at different scales10.1088/0029-5515/54/8/086001 ↗
8. Irradiation hardening of pure tungsten exposed to neutron irradiation10.1016/j.jnucmat.2016.08.024 ↗
9. Developing structural, high-heat flux and plasma facing materials for a near-term DEMO fusion power plant: the EU assessment10.1016/j.jnucmat.2014.06.014 ↗
10. Swelling in neutron irradiated tungsten and tungsten-25 percent rhenium10.1016/0036-9748(74)90304-4 ↗
11. Rate theory cluster dynamics simulations including spatial correlations within displacement cascades10.1103/PhysRevB.86.054113 ↗
12. Recovery temperatures of defects in tungsten created by self-implantation10.1016/j.jnucmat.2014.12.005 ↗
13. First temperature stage evolution of irradiation-induced defects in tungsten studied by positron annihilation spectroscopy10.1016/j.jnucmat.2008.03.002 ↗
14. Annealing of radiation-induced damage in tungsten under and after irradiation with 20 MeV self-ions10.1016/j.jnucmat.2014.04.011 ↗
15. Enhancement of deuterium retention in damaged tungsten by plasma-induced defect clustering10.1088/1741-4326/aa856c ↗
16. High temperature recovery of radiation defects in tungsten and its effect on deuterium retention
17. Vacancy cluster growth and thermal recovery in hydrogen-irradiated tungsten10.1016/j.jnucmat.2020.152017 ↗
18. Defect annealing in heavy-ion irradiated tungsten: long-time thermal evolution of saturated displacement damage at different temperatures10.1016/j.jnucmat.2023.154454 ↗
19. Electron microscopy observations of radiation damage in irradiated and annealed tungsten10.1016/j.nimb.2014.07.043 ↗
20. The influence of the annealing temperature on deuterium retention in self-damaged tungsten10.1088/0031-8949/T167/1/014031 ↗
21. Deuterium retention in tungsten simultaneously damaged by high energy W ions and loaded by D atoms
22. Stabilization of defects by the presence of hydrogen in tungsten: simultaneous W-ion damaging and d-atom exposure10.1088/1741-4326/aaec97 ↗
23. “TMAP7: tritium Migration Analysis Program,” User Manual, Idaho National Laboratory, INEEL/EXT-04-02352
24. W. Moller, Tech. Rep. IPP 9/44 Max-Planck-Institut Fur Plasmaphysik, 1983. Garching, Germany.
25. Baskes · 1983
26. Macroscopic rate equation modeling of trapping/detrapping of hydrogen isotopes in tungsten materials10.1016/j.jnucmat.2015.06.041 ↗
27. Modeling and simulation for surface helium effect on hydrogen isotopes diffusion and trapping/detrapping behavior in plasma facing materials10.1016/j.jnucmat.2020.152227 ↗
28. Deuterium uptake, desorption and sputtering from W(110) surface covered with oxygen10.1088/1741-4326/ad2a29 ↗
29. Mechanism of hydrogen isotope exchange for tritium removal in plasma-facing materials: a multi-scale investigation10.1088/1741-4326/ad280b ↗
30. Influence of helium bubbles location on hydrogen isotope retention and exchange behavior in plasma-facing materials: a numerical simulation investigation
31. Modeling the Co-permeation of hydrogen isotopes through metals in all rate-limited regimes10.1016/j.jnucmat.2024.155290 ↗
32. Modelling neutron damage effects on tritium transport in tungsten10.1088/1741-4326/ad56a0 ↗
33. Simulation of defect evolution in tungsten during annealing by developing a vacancy and interstitial-type defect evolution model
34. Hydrogen trapping models in steel10.1007/s11663-000-0032-0 ↗
35. SRIM - the stopping and range of ions in matter10.1016/j.nimb.2010.02.091 ↗
36. Investigating the formation mechanism of void lattice in tungsten under neutron irradiation: from collision cascades to ordered nanovoids10.1016/j.actamat.2021.117239 ↗
37. Annealing effects on deuterium retention behavior in damaged tungsten10.1016/j.nme.2016.06.012 ↗
38. Stability of small vacancy clusters in tungsten by molecular dynamics10.1016/j.nimb.2019.11.044 ↗
39. The damage depth profile effect on hydrogen isotope retention behavior in heavy ion irradiated tungsten10.1016/j.fusengdes.2017.05.141 ↗
40. Effects of helium bombardment on the deuterium behavior in tungsten10.1016/S0022-3115(02)01178-9 ↗
41. High temperature annealing of ion irradiated tungsten10.1016/j.actamat.2015.01.067 ↗
42. Defect evolution in single crystalline tungsten following low temperature and low dose neutron irradiation10.1016/j.jnucmat.2015.12.040 ↗
43. Role of hydrogen in stability and mobility of vacancy clusters in tungsten10.1007/s42864-022-00151-8 ↗
44. Low-energy particle interaction at carbon nanowalls on W surface10.1016/j.jnucmat.2009.01.281 ↗
45. Effect of D on the evolution of radiation damage in W during high temperature annealing10.1088/1741-4326/abaff6 ↗
46. Reduced defect recovery in self-ion damaged W due to simultaneous deuterium exposure during annealing10.1088/1741-4326/ac4773 ↗
47. Understanding why dislocation loops are visible in transmission electron microscopy: the tungsten case10.1016/j.jnucmat.2021.153122 ↗