Identification of NpO2+x in the binary Np-O system

In contrast to UO2 and PuO2, there is no consensus on the existence of mixed valence NpO2+x, resulting in a gap between NpO2 and Np2O5 (the highest binary oxide of Np) in the Np-O phase diagram. We now show NpO2+x via Np LIII Extended X-ray Absorption Fine Structure (EXAFS) spectra of three samples of NpO2 that, analogous to U and Pu, exhibit multisite Np-O distributions with varying numbers of oxygen atoms at 1.87–1.91 A. This is supported by the diffraction pattern of the sample with the largest amount of this oxo-type species that can be refined with both the simple fluorite structure and a trigonal one related to α-U4O9. The implied Np(V)-bridging oxo moieties as well as possible indications of OH¯ found by detailed EXAFS analysis suggest that NpO2+x more closely resembles PuO2+x than UO2+x. An additional common characteristic suggested by the EXAFS and X-Ray Diffraction (XRD) is the phase separation into NpO2 and what would be previously unreported Np4O9(–δ), indicative of O clustering.