In situ resistivity measurements of RAFM base alloys at cryogenic temperatures: The effect of proton irradiation

A four-probe technique for measurement of electrical resistance on low-temperature ion-irradiated metallic sheets is described. The design, temperature control system, preparation method of samples and the resistivity measurements are described in detail. The resistivity recovery (RR) curve has been measured on a Fe-5%Cr model alloy irradiated with 5 MeV protons. The procedure to obtain the RR derivative curve is outlined and experimental errors are identified and quantified. Special care has been taken to use a sample with very low impurity content and low dislocation density (1.2 ?? 10 8 cm-2). Thus, effects in recovery spectrum of the Fe-5%Cr alloy are only due to the presence of Cr and irradiation defects, which will be mainly Frenkel Pairs (FPs) given that the mean energy of the Primary Knock-on Atoms (PKA) is close to 0.35 keV. The results obtained for the Fe-5%Cr under 5 MeV proton irradiation are found to be in overall agreement with previous experimental measurements performed under electron irradiation although some differences appear probably due to the different spatial distribution of the created defects and the higher temperature resolution of annealing steps. The RR spectrum obtained reveals the appearance of the structure of stages I and II and also a partial suppression of the stage III peak with respect to previous results obtained after electron irradiation. The stage III suppression is explained as a superposition of vacancy recombination effects and short-range ordering (SRO) effects which are apparently dependent on the spatial distribution of defects created during irradiation. Moreover, recombination phenomena are observed beyond stage III up to 500 K.