Feasibility tests of nickel as a containment material of molten Li2O-LiCl salt containing Li metal at 650 °C during electrolytic reduction

Abstract In this study, we investigated the feasibility of nickel (Ni) as a material to contain molten Li 2 O-LiCl salt containing lithium (Li) metal at 650 °C as an electrolyte during the electrolytic reduction process of pyroprocessing (also known as oxide reduction, OR). First, the behaviors of Ni in four different LiCl salts (0.1 wt% Li-LiCl, 1 and 8 wt% Li 2 O-LiCl, and 8 wt% Li 2 O-0.1 wt% Li-LiCl) in an argon atmosphere were examined through immersion tests. Then, Ni was used as a vessel material for five consecutive OR runs of simulated oxide fuel using 1.0 wt% Li 2 O-LiCl salt. The tested Ni was analyzed by microbalance, X-ray diffraction, scanning electron microscopy, and energy-dispersive X-ray spectroscopy. Concentrations of Ni in the salt were measured using inductively coupled plasma atomic emission spectroscopy. No corrosion product of Ni, except Cr 2 Ni 3 , was observed on the Ni used for both the salt-immersion tests and the OR runs because the Ni was not exposed to oxygen gas. However, leaching of Ni in the OR salt containing excessive Li metal was observed. Therefore, Ni can be used as the salt containment material in the OR process when excessive Li metal and oxygen gas in the salt are maintained at low levels.