Formation and deposition of platinum nanoparticles under boiling water reactor conditions

Stress corrosion cracking (SCC) is a well-known degradation mechanism for components of boiling water reactors (BWRs). Therefore the mitigation of SCC is important for ensuring the integrity of the reactor system. Noble metal chemical application (NMCA) has been developed by General Electric to mitigate SCC and reduce the negative side-effects of hydrogen water chemistry used initially for SCC mitigation. NMCA is now widely applied as an online process (OLNC) during power operation. However, the understanding of the parameters that control the formation and deposition of the noble metal (Pt) particles in a BWR was still incomplete. To fill this knowledge gap, systematic studies on the formation and deposition behaviour of Pt particles in simulated and real BWR environment were performed in the framework of a research project at PSI. The present paper summarizes the most important findings. Experiments in a sophisticated high-temperature water loop revealed that the flow conditions, water chemistry, the Pt injection rate, and the pre-conditioning of the stainless steel surfaces have an impact on the Pt deposition behaviour. Slower Pt injection rates and stoichiometric excess of H2 over O2 produce smaller particles, which may increase the efficiency of the OLNC technique in mitigating SCC. Surfaces with a well-developed oxide layer retain more Pt particles. Furthermore, the pre- and post-OLNC exposure times play an important role for the Pt deposition on specimens exposed at the KKL power plant. Redistribution of Pt in the plant takes place, but most of the Pt apparently does not redeposit on the steel surfaces in the reactor system. Comparison of lab and plant results also demonstrated that plant OLNC applications can be simulated reasonably well on the lab scale.