On flux effects in a low alloy steel from a Swedish reactor pressure vessel

Magnus Boåsen, Pål Efsing, Ulla Ehrnstén

Publisher page

Abstract

This study aims to investigate the presence of Unstable Matrix Defects in irradiated pressure vessel steel from weldments of the Swedish PWR Ringhals 4 (R4). Hardness tests have been performed on low flux (surveillance material) and high flux (Halden reactor) irradiated material samples in combination with heat treatments at temperatures of 330, 360 and 390 °C in order to reveal eventual recovery of any hardening features induced by irradiation. The experiments carried out in this study could not reveal any hardness recovery related to Unstable Matrix Defects at relevant temperatures. However, a difference in hardness recovery was found between the low and the high flux samples at heat treatments at higher temperatures than expected for the annihilation of Unstable Matrix Defects–the observed recovery is here attributed to differences of the solute clusters formed by the high and low flux irradiations.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Fusion materials and technologies · Microstructure and Mechanical Properties of Steels

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (23)

Show source-provided references
1. Microstructural evolution in reactor pressure vessel steels10.1016/0022-3115(93)90079-E ↗
2. Recent progress in understanding reactor pressure vessel steel embrittlement10.1080/10420159808229676 ↗
3. Embrittlement of nuclear reactor pressure vessels10.1007/s11837-001-0081-0 ↗
4. Odette · 1993
5. Advanced models of LWR pressure vessel embrittlement for low flux-high fluence conditions
6. Neutron flux and annealing effects on irradiation hardening of RPV materials10.1016/j.jnucmat.2011.06.012 ↗
7. Confirmatory investigations on the flux effect and associated unstable matrix damage in RPV material exposed to high neutron fluence10.1016/j.jnucmat.2013.02.029 ↗
8. International Atomic Energy Agency (IAEA) · 2005
9. Analysis of the ductile-to-brittle transition temperature shift in a commercial power plant with high nickel containg weld material
10. Atom probe tomography characterizations of high nickel, low copper surveillance RPV welds irradiated to high fluences10.1016/j.jnucmat.2013.01.312 ↗
11. Post-irradiation annealing of Ni-Mn-Si-enriched clusters in a neutron irradiated RPV steel weld using atom probe Tomography10.1016/j.jnucmat.2015.01.027 ↗
12. Radiation-induced precipitation in a ferritic model alloy: an experimental and theoretical study10.1016/j.actamat.2013.07.008 ↗
13. Formation and evolution of MnNi clusters in neutron irradiated dilute Fe alloys modelled by a first principle-based AKMC method10.1016/j.jnucmat.2012.03.033 ↗
14. On the thermal stability of late blooming phases in reactor pressure vessel steels: an atomistic study10.1016/j.jnucmat.2013.08.018 ↗
15. Monte Carlo study of decorated dislocation loops in FeNiMnCu model alloys10.1016/j.jnucmat.2014.05.051 ↗
16. E185–73 Surveillance tests for nuclear reactor vessels
17. P. Efsing, J. Rouden and P. Nilsson, “Flux Effects on Radiation Induced Aging Behaviour of Low Alloy Steel Weld Material with High Nickel and Manganese Content,” in ASTM 26th Symposium on Effects of Radiation on Nuclear Materials, Indianapolis, 2013.10.1520/STP157220130112 ↗
18. E384–11 standard test method for knoop and Vickers hardness of materials
19. Evolution of the nanostructure of VVER-1000 RPV materials under neutron irradiation and post irradiation annealing10.1016/j.jnucmat.2009.01.299 ↗
20. Effect of neutron flux on the characteristics of irradiation-induced nanofeatures and hardening in pressure vessel steels10.1016/j.actamat.2015.11.027 ↗
21. Dohi · 2010
22. Soneda · 2014 · vol. 8
23. Modeling the microstructural evolution in bcc-Fe during irradiation using kinetic Monte Carlo computer simulation10.1016/j.jnucmat.2003.08.021 ↗