Comparison of delayed hydride cracking behavior of two zirconium alloys
Source abstract
Abstract
Abstract Delayed hydride cracking (DHC) is an important failure mechanism that may occur in Zr alloys during service in water-cooled reactors. Two conditions must be attained to initiate DHC from a crack: the stress intensity factor must be higher than a threshold value called K IH and, hydrogen concentration must exceed a critical value. Currently the pressure tubes for CANDU reactor are fabricated from Zr–2.5Nb. In this paper the critical hydrogen concentration for DHC and the crack velocity of a developmental pressure tube, Excel, was evaluated and compared with that of Zr–2.5Nb. The DHC velocity values measured in Excel were higher than usually reported in Zr–2.5Nb. Due to the higher hydrogen solubility limits in Excel, its critical hydrogen concentration for DHC initiation is 10–50 wppm over that of Zr–2.5Nb in the range of 150–300 °C.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Nuclear Materials and Properties · Fusion materials and technologies · Nuclear reactor physics and engineering
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (20)
Show source-provided references
1. IAEA-TECDOC-1410, Delayed Hydride Cracking in Zirconium Alloys in Pressure Tube Nuclear Reactors, IAEA, Vienna, October 2004.
2. Measurement of rates of delayed hydride cracking (DHC) in Zr–2.5 Nb alloys – an IAEA coordinated research project10.1520/JAI101091 ↗
3. Cracking of hydride-forming metals and alloys
4. Shi · J. Nucl. Mater. · 1994 · 208 · 23210.1016/0022-3115(94)90332-8 ↗
5. Shi · J. Nucl. Mater. · 1994 · 218 · 3010.1016/0022-3115(94)00368-8 ↗
6. Measurement of effective solvus of hydrogen in Zr–2.5wt% Nb using acoustic emission
7. Shi · J. Nucl. Mater. · 1995 · 218 · 18910.1016/0022-3115(94)00405-6 ↗
8. McRae · J. Nucl. Mater. · 2010 · 396 · 13010.1016/j.jnucmat.2009.08.019 ↗
9. Ells · J. Alloy Compd. · 1995 · 231 · 78510.1016/0925-8388(95)01718-6 ↗
10. B.A. Cheadle, R.A. Holt, V. Fidleris, A.R. Causey, V.F. Urbanic. High-Strength, Creep-Resistant Excel Pressure Tubes, Zirconium in the Nuclear Industry, in: D.G. Franklin, (Ed.), Fifth Conference, ASTM STP 754, American Society for Testing and Materials, 1982, pp. 193.10.1520/STP37055S ↗
11. Ibrahim · Can. Metall. Quart. · 1985 · 24 · 18110.1179/cmq.1985.24.3.273 ↗
12. Cirimello · J. Nucl. Mater. · 2006 · 350 · 13510.1016/j.jnucmat.2005.12.002 ↗
13. Khatamian · J. Alloy Compd. · 1995 · 231 · 48810.1016/0925-8388(95)01867-0 ↗
14. Mieza · J. Mater. Sci. · 2008 · 43 · 494510.1007/s10853-008-2723-x ↗
15. ASTM E 1820–08a, Standard Test Method for Measurement of Fracture Toughness.
16. Pan · J. Nucl. Mater. · 1996 · 228 · 22710.1016/S0022-3115(95)00217-0 ↗
17. Amouzouvi · Metall. Trans. · 1987 · 18A · 168710.1007/BF02646200 ↗
18. Mieza · J. Nucl. Mater. · 2011 · 411 · 15010.1016/j.jnucmat.2011.01.101 ↗
19. Effects of crack tip stress states and hydride–matrix interaction stresses on delayed hydride cracking10.1007/BF02647211 ↗
20. Dilation of h.c.p. zirconium by interstitial deuterium10.1016/0001-6160(85)90098-7 ↗