Dry bag isostatic pressing for improved green strength of surrogate nuclear fuel pellets

Abstract Dry bag isostatic pressing is proposed for mass production of nuclear fuel pellets. Dry bag isostatically pressed rods of a fuel surrogate (95% CeO2–5% HfO2) 200 mm long by 8 mm diameter were cut into pellets using a wire saw. Four different binders and CeO2 powder obtained from two different sources were investigated. The strength of the isostatically pressed pellets for all binder systems measured by diametral compression was about 50% higher than pellets produced by uniaxial dry pressing at the same pressure. It was proposed that the less uniform density of uniaxially pressed pellets accounted for the lower strength. The strength of pellets containing CeO2 powder with significantly higher moisture content was five times higher than pellets containing CeO2 powder with a low moisture content even though they were 25% less dense. Capillary pressure of the moisture was thought to supply the added binding strength.