Irradiation and post-irradiation examination of uranium-free nitride fuel

Two identical Phénix-type 15-15Ti steel pinlets each containing a 70 mm Pu _0.3Zr _0.7 N fuel stack in a 1-bar helium atmosphere have been irradiated in the HFR Petten at medium high linear power (46–47 kW/m at BOL) and an average cladding temperature of 505 °C. The pins were irradiated to a plutonium burn-up of 9.7% (88 MWd/kg _HM ) in 170 full power days. Both pins remained fully intact. Post-irradiation examination performed at NRG and PSI showed that the overall swelling rate of the fuel was 0.92 vol-%/%FIHMA. Fission gas release was 5–6%, while helium release was larger than 50%. No fuel restructuring was observed, and only mild cracking. EPMA measurements show a burn-up increase toward the pellet edge of up to 4 times. All investigated fission products except to some extent the noble metals were found to be evenly distributed over the matrix, indicating good solubility. Local formation of a secondary phase with high Pu content and hardly any Zr was observed. A general conclusion of this investigation is that ZrN is a suitable inert matrix for burning plutonium at high destruction rates.