Modeling thermal and irradiation-induced swelling effects on the integrity of Ti3SiC2/SiC joints
Source abstract
Abstract
Abstract Previously, results for CVD-SiC joined by a solid state displacement reaction to form a dual-phase SiC/MAX phase joint subsequently irradiated at 800 °C to 5 dpa indicated some cracking in the joint. This paper elucidates the cracking origin by developing a model that accounts for differential thermal expansion and irradiation-induced swelling between the substrate and joint materials by using a continuum damage mechanics approach with support from micromechanical modeling. Damage accumulation in joined specimens irradiated at four temperatures (300 °C, 400 °C, 500 °C and 800 °C) is analyzed. We assume the experimental irradiation dose is sufficient to cause saturation swelling in SiC. The analyses indicate that the SiC/MAX joint survives irradiation-induced swelling at all the irradiation temperatures considered. The joint experiences only minor damage when heated to and irradiated at 800 °C as well as cooling to room temperature. The prediction agrees with the experimental findings available for this case. However, the joint heated to 300 °C suffers severe damage during irradiation-induced swelling at this temperature, and additional damage after cooling to room temperature. Irradiation at 400 °C and subsequent cooling to room temperature produced similar damage to the irradiation 300 °C case, but to a lesser extent. The joint heated to 500 °C and irradiated at this temperature suffered only very minor damage, but further moderate damage occurred after cooling to room temperature.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · MXene and MAX Phase Materials · Aluminum Alloys Composites Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (27)
Show source-provided references
1. Katoh · J. Nucl. Mater. · 2014 · 448 · 49710.1016/j.jnucmat.2013.10.002 ↗
2. Radhakrishnan · Scr. Mater. · 1996 · 34 · 180910.1016/1359-6462(95)00663-X ↗
3. Henager · J. Nucl. Mater. · 2011 · 417 · 37510.1016/j.jnucmat.2010.12.084 ↗
4. Henager · J. Nucl. Mater. · 2015 · 466 · 25310.1016/j.jnucmat.2015.07.044 ↗
5. Koyanagi · J. Nucl. Mater. · 2017 · 488 · 15010.1016/j.jnucmat.2017.03.017 ↗
6. Nguyen · J. Am. Ceram. Soc. · 2006 · 89 · 135810.1111/j.1551-2916.2005.00874.x ↗
7. Snead · J. Nucl. Mater. · 2007 · 371 · 32910.1016/j.jnucmat.2007.05.016 ↗
8. Ben-Belgacem · J. Nucl. Mater. · 2014 · 447 · 12510.1016/j.jnucmat.2014.01.006 ↗
9. Lemaître · 1985
10. Maugin · 1992
11. Lemaitre · 2002 · 235
12. Renard · Compos. Sci. Technol. · 1993 · 46 · 2910.1016/0266-3538(93)90078-U ↗
13. Tvergaard · Int. J. Fract. · 1986 · 31 · 18310.1007/BF00018927 ↗
14. Nguyen · Int. J. Damage Mech. · 2010 · 19 · 69110.1177/1056789509338319 ↗
15. Barsoum · Acta Mater. · 2006 · 54 · 275710.1016/j.actamat.2006.02.019 ↗
16. Manoun · J. Am. Ceram. Soc. · 2005 · 88 · 348910.1111/j.1551-2916.2005.00642.x ↗
17. Barsoum · J. Phys. Chem. Solids · 1999 · 60 · 42910.1016/S0022-3697(98)00313-8 ↗
18. Gao · Mater. Sci. Engn A · 2016 · 676 · 19710.1016/j.msea.2016.08.098 ↗
19. Mori · Acta Metall. · 1973 · 21 · 57110.1016/0001-6160(73)90064-3 ↗
20. Benveniste · Mech. Mater. · 1987 · 6 · 14710.1016/0167-6636(87)90005-6 ↗
21. Eshelby · Proc. R. Soc. Lond. · 1959 · 252 · 561
22. Nguyen · 2010
23. Kachanov · Izv. Akad. Nauk. SSSR · 1958 · 8 · 26
24. Advani · J. Rheol. · 1987 · 31 · 75110.1122/1.549945 ↗
25. Ruh · Am. Ceram. Soc. Bull. · 1985 · 64 · 1368
26. Ang · J. Nucl. Mater. · 2017 · 483 · 4410.1016/j.jnucmat.2016.10.036 ↗
27. Yutai · J. Nucl. Mater. · 2013 · 434 · 14110.1016/j.jnucmat.2012.11.035 ↗