Generation and development of damage in double forged tungsten in different combined regimes of irradiation with extreme heat loads

Abstract Armour materials in fusion devices, especially in the region of divertor, are exposed to a continuous heat and particle load. In addition, several off-normal events can reach the material during a work session. Calculations show that the effects of plasma and heat during such events can lead to cracking, erosion and detachment of the armour material. On the other hand, mutual and combined influences of different kinds of heat and particle loads can lead to the amplification of defects or vice versa, to the mitigation of damages. Therefore, the purpose of the study is to investigate the plasma induced damages on samples of double forged tungsten, which is considered a potential candidate for armour material of future tokamak's divertor. The combined effect of different kinds of plasma induced damages was investigated and analysed in this research. The study was conducted by irradiating the samples in various irradiation regimes twice, to observe the accumulation of the damages. Afterwards the analysis of micro-topography, scanning electron microscopy images and electrical conductivity measurements was used. Results indicate that double-forging improved the tungsten's durability to irradiation. Nevertheless, powerful pulses lead to significant damage of the sample, which will lead to further deterioration in the bulk. Although the average micro-roughness on the sample's surface does not change, the overall height/depth ratios can change.