Effects of manufacturing process on impact properties and microstructures of ODS steels

Abstract Oxide dispersion strengthened (ODS) steels are notable advanced alloys with durability to a high-temperature and high-dose neutron irradiation environment because of their good swelling resistance and mechanical properties under neutron irradiation. 9–12Cr-ODS martensite steels have been developed in the Japan Atomic Energy Agency as the primary candidate material for the fast reactor fuel cladding tubes. They would also be good candidates for the fusion reactor blanket material which is exposed to high-dose neutron irradiation. In this work, modification of the manufacturing process of 11Cr-ODS steel was carried out to improve its impact property. Two types of 11Cr-ODS steels were manufactured: pre-mix and full pre-alloy ODS steels. Miniature Charpy impact tests and metallurgical observations were carried out on these steels. The impact properties of full pre-alloy ODS steels were shown to be superior to those of pre-mix ODS steels. It was demonstrated that the full pre-alloy process noticeably improved the microstructure homogeneity (i.e. reduction of inclusions and pores).