TEM/STEM study of Zircaloy-2 with protective FeAl(Cr) layers under simulated BWR environment and high-temperature steam exposure
Source abstract
Abstract
Abstract FeAl(Cr) thin-film depositions on Zircaloy-2 were studied using transmission electron microscopy (TEM) and scanning transmission electron microscopy (STEM) with respect to oxidation behavior under simulated boiling water reactor (BWR) conditions and high-temperature steam. Columnar grains of FeAl with Cr in solid solution were formed on Zircaloy-2 coupons using magnetron sputtering. NiFe2O4 precipitates on the surface of the FeAl(Cr) coatings were observed after the sample was exposed to the simulated BWR environment. High-temperature steam exposure resulted in grain growth and consumption of the FeAl(Cr) layer, but no delamination at the interface. Outward Al diffusion from the FeAl(Cr) layer occurred during high-temperature steam exposure (700 °C for 3.6 h) to form a 100-nm-thick alumina oxide layer, which was effective in mitigating oxidation of the Zircaloy-2 coupons. Zr intermetallic precipitates formed near the FeAl(Cr) layer due to the inward diffusion of Fe and Al. The counterflow of vacancies in response to the Al and Fe diffusion led to porosity within the FeAl(Cr) layer.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Nuclear Materials and Properties · Nuclear reactor physics and engineering · Fusion materials and technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (49)
Show source-provided references
1. Preliminary assessment of the performance of SiC-based accident tolerant fuel in commercial LWR systems
2. Cladding for high-performance fuel10.1016/j.pnucene.2011.10.008 ↗
3. Long-term corrosion behavior of CVD SiC in 360°C water and 400°C steam10.1016/j.jnucmat.2013.07.058 ↗
4. Thermo-mechanical analysis of LWR SiC/SiC composite cladding10.1016/j.jnucmat.2014.01.006 ↗
5. Advanced oxidation-resistant iron-based alloys for LWR fuel cladding10.1016/j.jnucmat.2013.06.041 ↗
6. A study of the oxidation of FeCrAl alloy in pressurized water and high-temperature steam environment10.1016/j.corsci.2015.02.027 ↗
7. Effect of steam on high temperature oxidation behaviour of alumina-forming alloys10.1179/0960340914Z.00000000058 ↗
8. OECD · 2013
9. Accident tolerant fuels for LWRs: a perspective10.1016/j.jnucmat.2013.12.005 ↗
10. Protection of zirconium by alumina- and chromia-forming iron alloys under high-temperature steam exposure10.1016/j.jnucmat.2013.03.006 ↗
11. Performance of iron–chromium–aluminum alloy surface coatings on Zircaloy 2 under high-temperature steam and normal BWR operating conditions10.1016/j.jnucmat.2015.11.037 ↗
12. Billot · 1993
13. Low-temperature oxidation of Zircaloy-2 in water10.1016/0022-3115(68)90176-1 ↗
14. Long-term corrosion of Zircaloy before and after irradiation10.1016/S0022-3115(99)00230-5 ↗
15. Transformations and cracks in zirconia films leading to breakaway oxidation of Zircaloy10.1016/j.actamat.2013.02.052 ↗
16. Growth and characterization of oxide layers on zirconium alloys10.1016/0022-3115(95)00233-2 ↗
17. Transmission electron microscopy examination of oxide layers formed on Zr alloys10.1016/j.jnucmat.2005.10.012 ↗
18. Transmission electron microscopy characterization of Zircaloy-4 and ZIRLO oxide layers10.1016/j.jnucmat.2014.09.073 ↗
19. Oxidation of Zircaloy-2 and Zircaloy-4 in water and lithiated water at 360°C10.1016/S0022-3115(01)00480-9 ↗
20. A comparison of the oxidation behavior of Fe-Cr-Al, Ni-Cr-Al and Co-Cr-Al alloys10.1007/BF00603481 ↗
21. The isothermal oxidation behaviour of Fe-Cr-Al and Fe-Cr-Al-Y alloys at 1200°C10.1016/S0010-938X(79)80110-9 ↗
22. Oxidation of FeCrAl alloys at 500–900°C in dry O210.1002/maco.200503882 ↗
23. Oxidation of FeCrAl foils at 500–900°C in dry O2 and O2 with 40% H2O10.3184/096034009X464311 ↗
24. Microstructural development of α-alumina scales developed on FeCrAl alloys10.1179/174328406X131091 ↗
25. High-temperature oxidation of FeCrAl alloys–influence of Al concentration on oxide layer characteristics10.1002/maco.200805186 ↗
26. The formation of aluminum oxide scales on high-temperature alloys10.1007/BF00666913 ↗
27. Pyrolytic carbon coating of Zircaloy-4 tubes at relatively low temperatures10.1016/S0022-3115(97)00214-6 ↗
28. The effect of Zircaloy-4 substrate surface condition on the adhesion strength and corrosion of SiC coatings10.1016/j.jnucmat.2005.05.016 ↗
29. Ceramic coating for corrosion (c3) resistance of nuclear fuel cladding10.1016/j.surfcoat.2015.08.062 ↗
30. Multilayer (TiN, TiAlN) ceramic coatings for nuclear fuel cladding10.1016/j.jnucmat.2016.05.021 ↗
31. Investigations of aluminum-doped self-healing Zircaloy surfaces in context of accident-tolerant fuel cladding research10.1007/s11665-016-2094-4 ↗
32. Development status of accident-tolerant fuel for light water reactors in Korea10.1016/j.net.2015.11.011 ↗
33. Protective coatings on zirconium-based alloys as accident-tolerant fuel (ATF) claddings10.1515/corrrev-2017-0010 ↗
34. The effect of oxide microstructure on kinetic transition in out-of-pile steam corrosion test for Zircaloy-2 and Nb-added Zircaloy-210.1080/18811248.2001.9715048 ↗
35. Detailed analysis of the microstructure of the metal/oxide interface region in Zircaloy-2 after autoclave corrosion testing
36. Multi-scale characterization of the metal-oxide interface of zirconium alloys
37. Point defects and transport in non-stoichiometric oxides: solved and unsolved problems10.1016/S0022-3697(97)00205-9 ↗
38. Uniform corrosion of FeCrAl alloys in LWR coolant environments10.1016/j.jnucmat.2016.06.047 ↗
39. Diffusion in α-Ti and Zr10.2320/matertrans.44.2 ↗
40. Equilibrium chemistry of nitrogen and potential-pH diagrams for the Fe-Cr-H2O system in BWR water10.1016/0022-3115(89)90447-9 ↗
41. Thermodynamics of formation of simple spinels10.1016/0022-1902(68)80475-0 ↗
42. Primary side crud sampling and characterization: how it may help to better maintain candu reactors
43. Structures and transformation mechanisms of the η, γ and θ transition aluminas10.1107/S0108768191002719 ↗
44. Birkholz · 2006
45. The oxidation of alumina-forming alloys10.4028/www.scientific.net/MSF.251-254.19 ↗
46. Growth and microstructure of α-Al2O3 on β-NiAl10.1149/1.2129965 ↗
47. The influence of yttrium additions on the oxide-scale adhesion to an iron-chromium-aluminum alloy10.1007/BF00612158 ↗
48. Microstructure, adhesion and growth kinetics of protective scales on metals and alloys10.1007/BF00656571 ↗
49. Response of Cr and Cr-Al coatings on Zircaloy-2 to high-temperature steam10.1016/j.jnucmat.2017.10.021 ↗