Effect of crystallite orientation and external stress on hydride precipitation and dissolution in Zr2.5%Nb
Source abstract
Abstract
Abstract Thermal cycling of Zr2.5%Nb pressure tubes specimens containing ∼100 wt ppm H between room temperature and 400 °C produces the dissolution and re-precipitation of zirconium hydride, with a distinctive hysteresis between these two processes. In this work, we have found that the details of the precipitation and dissolution depend on the actual orientation of the α-Zr grains where hydride precipitation takes place. In situ synchrotron X-ray diffraction experiments during such thermal cycles have provided information about hydride precipitation specific to the two most important groups of α-Zr phase orientations, namely crystallites having c -axes parallel ( m Hoop ) and tilted by ∼20° ( m Tilted ) from the tube hoop direction. The results indicate that hydrides precipitate at slightly higher temperatures (∼5 °C), and dissolve at consistently higher temperatures (∼15 °C) in m Tilted grains than in m Hoop grains. Moreover, application of a tensile stress along the tube hoop direction results in two noticeable effects in hydride precipitation. Firstly, it shifts hydride precipitation towards higher temperatures, at a rate of ∼(0.08 ± 0.02) °C/MPa for hydrides precipitated in the m Hoop grains. Secondly, it produces a redistribution of hydrogen between grains of different orientations, increasing hydride precipitation on those α-Zr grains having their c -axes stretched by the external load. A detailed analysis of the diffracted signal shows that such redistribution occurs during the precipitation stage, as a result of changes in the precipitation temperatures for different grain orientations.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Nuclear Materials and Properties · Fusion materials and technologies · Nuclear reactor physics and engineering
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (38)
Show source-provided references
1. Fukai · 2005
2. Puls · Acta Metall. · 1984 · 32 · 125910.1016/0001-6160(84)90133-0 ↗
3. Puls · Acta Metall. · 1991 · 29 · 196110.1016/0001-6160(81)90033-X ↗
4. Erickson · J. Nucl. Mater. · 1964 · 13 · 25410.1016/0022-3115(64)90046-7 ↗
5. Paton · Metall. Mater. Trans. B · 1971 · 2 · 279110.1007/BF02813253 ↗
6. Birnbaum · J. Less Common Metals · 1976 · 49 · 35710.1016/0022-5088(76)90048-5 ↗
7. Flanagan · Scripta Metall. · 1981 · 15 · 10910.1016/0036-9748(81)90148-4 ↗
8. Perovic · Acta Metall. · 1983 · 31 · 138110.1016/0001-6160(83)90008-1 ↗
9. Leitch · Metall. Mater. Trans. A · 1992 · 3 · 79710.1007/BF02675557 ↗
10. Lufrano · J. Mech. Phys. Solids · 1996 · 44 · 17910.1016/0022-5096(95)00075-5 ↗
11. Simpson · J. Nucl. Mater. · 1974 · 52 · 28910.1016/0022-3115(74)90174-3 ↗
12. Pardee · Metall. Mater. Trans. A · 1980 · 11 · 139110.1007/BF02653494 ↗
13. Puls · 2012
14. McRae · J. Nucl. Mater. · 2010 · 396 · 13010.1016/j.jnucmat.2009.08.019 ↗
15. B.F. Kammenzind, B.M. Berquist, R. Bajaj, P.H. Kreyns, D.G. Franklin, in: 12th Intern. Symp. on Zirconium in Nuclear Industry, ASTM STP 1354, 2000, pp. 196–233.10.1520/STP14301S ↗
16. Vicente-Alvarez · Acta Mater. · 2012 · 60 · 689210.1016/j.actamat.2012.07.029 ↗
17. Haeffner · Mater. Sci. Eng. A · 2005 · 399 · 12010.1016/j.msea.2005.02.023 ↗
18. Holt · J. Nucl. Mater. · 1985 · 135 · 24610.1016/0022-3115(85)90084-4 ↗
19. Holt · J. Nucl. Mater. · 2004 · 335 · 52010.1016/j.jnucmat.2004.07.043 ↗
20. Carpenter · J. Nucl. Mater. · 1973 · 48 · 26410.1016/0022-3115(73)90022-6 ↗
21. Giroldi · J. Alloys Compd. · 2009 · 474 · 14010.1016/j.jallcom.2008.06.104 ↗
22. Zanellato · J. Nucl. Mater. · 2012 · 420 · 53710.1016/j.jnucmat.2011.11.009 ↗
23. MacEwen · Acta Metall. · 1985 · 33 · 75310.1016/0001-6160(85)90098-7 ↗
24. Daum · J. Nucl. Mater. · 2009 · 392 · 45310.1016/j.jnucmat.2009.04.004 ↗
25. I.G. Ritchie, K. Sprungmann, Atomic Energy of Canada, Report 1983 AECL-7806.
26. Khatamian · J. Nucl. Mater. · 2008 · 372 · 10610.1016/j.jnucmat.2007.02.010 ↗
27. Hellouin de Menibus · J. Nucl. Mater. · 2013 · 440 · 16910.1016/j.jnucmat.2013.04.039 ↗
28. Vicente-Alvarez · Acta Mater. · 2011 · 59 · 221010.1016/j.actamat.2010.12.024 ↗
29. Kirchheim · Acta Metal. · 1987 · 35 · 289910.1016/0001-6160(87)90288-4 ↗
30. Coleman · Scripta Metall. · 1983 · 17 · 7710.1016/0036-9748(83)90074-1 ↗
31. Eadie · Scripta Metall. · 1989 · 23 · 186510.1016/0036-9748(89)90473-0 ↗
32. Shi · Scripta Mater. · 1999 · 41 · 111510.1016/S1359-6462(99)00272-9 ↗
33. Zuzek · Bull. Alloy Phase Diagr. · 1990 · 11 · 38510.1007/BF02843318 ↗
34. Weatherly · Acta Metall. · 1981 · 29 · 50110.1016/0001-6160(81)90074-2 ↗
35. Barrow · J. Nucl. Mater. · 2013 · 432 · 36610.1016/j.jnucmat.2012.08.003 ↗
36. Hardie · J. Nucl. Mater. · 1975 · 55 · 110.1016/0022-3115(75)90132-4 ↗
37. Marshall · J. Nucl. Mater. · 1967 · 24 · 4910.1016/0022-3115(67)90079-7 ↗
38. Ells · J. Nucl. Mater. · 1970 · 35 · 30610.1016/0022-3115(70)90214-X ↗