Uranium nitride as LWR TRISO fuel: Thermodynamic modeling of U–C–N
Source abstract
Abstract
Abstract TRISO coated particle fuel is envisioned as a next generation replacement for current urania pellet fuel in LWR applications. To obtain adequate fissile loading the kernel of the TRISO particle will likely need to be UN instead of UO2. In support of the necessary development effort for this new fuel system, an assessment of phase regions of interest in the U–C–N system was undertaken as the fuel will be prepared by the carbothermic reduction of the oxide followed by nitriding, will be in equilibrium with carbon within the TRISO particle, and will react with minor actinides and fission products. The phase equilibria and thermochemistry of the U–C–N system is reviewed, including nitrogen pressure measurements above various phase fields. Measurements were used to confirm an ideal solution model of UN and UC adequately represents the UC1−xNx phase. Agreement with the data was significantly improved by effectively adjusting the Gibbs free energy of UN by +12 kJ/mol. This also required adjustment of the value for the sesquinitride by +17 kJ/mol to obtain agreement with phase equilibria. The resultant model together with reported values for other phases in the system was used to generate isothermal sections of the U–C–N phase diagram. Nitrogen partial pressures were also computed for regions of interest.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Nuclear Materials and Properties · Nuclear reactor physics and engineering · Thermodynamic and Structural Properties of Metals and Alloys
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (27)
Show source-provided references
1. K.A. Terrani, L.L. Snead, J.C. Gehin, J. Nucl. Mater., accepted for publication.
2. Terrani · J. Nucl. Mater. · 2012 · 426 · 26810.1016/j.jnucmat.2012.03.049 ↗
3. Austin · BMI-1272 · 1958
4. J.M. Leitnaker, Thermodynamics of Nuclear Materials, 1967, IAEA, 1968, p. 317.
5. T. Sano, M. Katsura, H. Kai, Thermodynamics of Nuclear Materials, 1967, IAEA, 1968, p. 301.
6. Henry · J. Am. Ceram. Soc. · 1969 · 52 · 53410.1111/j.1151-2916.1969.tb09159.x ↗
7. Naomidis · J. Nucl. Mater. · 1970 · 34 · 23010.1016/0022-3115(70)90131-5 ↗
8. Ikeda · J. Nucl. Mater. · 1976 · 59 · 10310.1016/0022-3115(76)90126-4 ↗
9. Cordfunke · J. Nucl. Mater. · 1979 · 79 · 27110.1016/0022-3115(79)90093-X ↗
10. Leitnaker · J. Am. Ceram. Soc. · 1970 · 53 · 47910.1111/j.1151-2916.1970.tb15994.x ↗
11. Prins · J. Nucl. Mater. · 1980 · 89 · 22110.1016/0022-3115(80)90057-4 ↗
12. Chevalier · J. Nucl. Mater. · 2001 · 288 · 10010.1016/S0022-3115(00)00713-3 ↗
13. Chevalier · J. Nucl. Mater. · 2000 · 280 · 13610.1016/S0022-3115(00)00043-X ↗
14. Bale · CALPHAD · 2002 · 26 · 3910.1016/S0364-5916(02)00035-4 ↗
15. D.R. Stull, H. Prophet, JANAF Thermochemical Tables, US Department of Commerce, Washington, 1985.
16. Olson · J. Phys. Chem. · 1963 · 67 · 95210.1021/j100798a525 ↗
17. P.A. Vozzela, M.A. DeCrescente, Thermodynamic Properties of Uranium Mononitride, Pratt and Whitney Aircraft Co., PWAC-479 UNCLAS, 1965.10.2172/4580380 ↗
18. Inouye · J. Am. Ceram. Soc. · 1968 · 51 · 610.1111/j.1151-2916.1968.tb11818.x ↗
19. Gingerich · J. Chem. Phys. · 1969 · 51 · 443310.1063/1.1671809 ↗
20. Alexander · Trans. Am. Nucl. Soc. · 1969 · 12 · 581
21. Bugl · J. Am. Ceram. Soc. · 1964 · 47 · 42510.1111/j.1151-2916.1964.tb14429.x ↗
22. A. Naoumidis, H.J. Stoecker, Thermodynamics of Nuclear Materials, 1967, IAEA, 1968, p. 287.
23. Sundman · CALPHAD · 1985 · 9 · 15310.1016/0364-5916(85)90021-5 ↗
24. Katsura · J. Nucl. Mater. · 1971 · 39 · 12510.1016/0022-3115(71)90017-1 ↗
25. Katsura · J. Nucl. Sci. Tech. · 1966 · 3 · 19410.1080/18811248.1966.9732305 ↗
26. Benz · J. Nucl. Mater. · 1969 · 31 · 9310.1016/0022-3115(69)90046-4 ↗
27. Katsura · J. Nucl. Mater. · 1970 · 36 · 16910.1016/0022-3115(70)90141-8 ↗