Microstructural characterization of EUROFER 97 during low-cycle fatigue

M.F. Giordana, I. Alvarez-Armas, A. Armas

Journal of Nuclear Materials· Volume 424· Issue 1-3
Publisher page

Abstract

Abstract The quenched and tempered reduced-activation ferritic/martensitic steel EUROFER 97 is one of the candidates for structural components of Generation IV nuclear power plants. The cyclic behaviour of this steel during isothermal plastic strain-controlled tests was investigated at room temperature and at 550 °C. Under low-cycle fatigue test this steel shows, after the first few cycles, a pronounced cyclic softening accompanied by microstructural changes such as the decrease of the free dislocation density inside the subgrain. The rate of softening increases with temperature being very pronounced at temperatures above 500 °C. The evolution of the flow stress during cycling was studied by analyzing the so-called “back” and “friction” stresses obtained from the hysteresis loops measured along the entire test. From the analysis of the hysteresis loops and corroborated by electron microscopy observations, it can be concluded that the strong cyclic softening observed is produced by the decrease exhibited by the friction stress. The Taylor coefficient was calculated measuring the evolution of the free dislocation density.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Fusion materials and technologies · High Temperature Alloys and Creep · Microstructure and Mechanical Properties of Steels

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (23)

Show source-provided references
1. R.L. Klueh, D.R. Harries, ASTM Mono3, West Conshohocken, PA USA, 2001.
2. Jones · Metall. Trans. · 1991 · 22A · 104910.1007/BF02661098 ↗
3. Armas · J. Nucl. Mater. · 2004 · 329-333 · 25210.1016/j.jnucmat.2004.04.045 ↗
4. Giordana · Key Eng. Mater. · 2011 · 465 · 35810.4028/www.scientific.net/KEM.465.358 ↗
5. Seeger · The Phys. Soc. London · 1955 · 328
6. Cottrell · 1953
7. Kuhlmann-Wilsdorf · Mater. Sci. Eng. · 1979 · 37 · 11110.1016/0025-5416(79)90074-0 ↗
8. Dickson · Mater. Sci. Eng. · 1984 · 64 · L710.1016/0025-5416(84)90083-1 ↗
9. Alvarez-Armas · Fatigue Fract. Eng. Mater. Struct. · 2003 · 26 · 2710.1046/j.1460-2695.2003.00584.x ↗
10. Fournier · Mater. Sci. Eng. A · 2006 · 437 · 18310.1016/j.msea.2006.08.086 ↗
11. Taylor · Proc. R. Soc. A · 1934 · 145 · 36210.1098/rspa.1934.0106 ↗
12. Amodeo · Acta Mater. · 2011 · 59 · 229110.1016/j.actamat.2010.12.020 ↗
13. Lavrentev · Mater. Sci. Eng. A · 1980 · 46 · 19110.1016/0025-5416(80)90175-5 ↗
14. Franciosi · Acta Metall. · 1980 · 28 · 27310.1016/0001-6160(80)90162-5 ↗
15. Courtney · 2000
16. Klaar · Prakt. Metallogr. · 1992 · 29 · 310.1515/pm-1992-290103 ↗
17. Thomas · 1964
18. Pešička · Acta Mater. · 2003 · 51 · 484710.1016/S1359-6454(03)00324-0 ↗
19. Marmy · J. Nucl. Mater. · 2008 · 377 · 5210.1016/j.jnucmat.2008.02.054 ↗
20. Sauzay · Mater. Sci. Eng. · 2008 · A410 · 483
21. J.R. Taylor, An introduction to Error Analysis: The study of uncertainties in Physical Measurements, University Science Book, second ed., 1997.
22. S. Naamane, Etude de la deformation plastique de la ferrite a basse temperature: simulations de dynamique des dislocation, PhD thesis, Universite Pierre et Marie Curie, 2008.
23. Madec · Scripta Mater. · 2008 · 58 · 76710.1016/j.scriptamat.2007.12.032 ↗