High thermal shock resistance of the hot rolled and swaged bulk W–ZrC alloys

Abstract The thermal shock (single shot) resistance and mechanical properties of the W–0.5wt% ZrC (WZC) alloys manufactured by ordinary sintering followed by swaging or rolling process were investigated. No cracks or surface melting were detected on the surface of the rolled WZC alloy plates after thermal shock at a power density of 0.66 GW/m2 for 5 ms, while primary intergranular cracks appear on the surface of the swaged WZC samples after thermal shock at a power density of 0.44 GW/m2 for 5 ms. Three point bending tests indicate that the rolled WZC alloy has a flexural strength of ∼2.4 GPa and a total strain of 1.8% at room temperature, which are 100% and 260% higher than those of the swaged WZC, respectively. The fracture energy density of the rolled WZC alloy is 3.23 × 107 J/m3, about 10 times higher than that of the swaged WZC (2.9 × 106 J/m3). The high thermal shock resistance of the rolled WZC alloys can be ascribed to their extraordinary ductility and plasticity.