Thermal stability of nano-structured ferritic alloy

P. Miao, G.R. Odette, T. Yamamoto, M. Alinger, D. Klingensmith

Journal of Nuclear Materials· Volume 377· Issue 1
Publisher page

Abstract

Abstract The excellent tensile and creep strength and the potential for managing radiation damage make nano-structured ferritic alloys (NFAs) promising candidates for high-temperature applications in spallation proton, advanced fission and fusion neutron environments. The thermal stability of NFAs is critical for such applications, hence, this has been investigated in a series of aging experiments on MA957 at 900 °C, 950 °C and 1000 °C for times up to 3000 h. Optical and transmission electron microscopy (TEM) studies showed the fine scale grain and dislocation structures are stable up to 1000 °C. TEM and small angle neutron scattering (SANS) showed that the nm-scale solute cluster-oxide features (NFs), that are a primary source of the high strength of NFAs, were stable at 900 °C and coarsened only slightly at 950 °C and 1000 °C. Porosity that developed during high-temperature aging was minimal at 900 °C and modest at 950 °C, but was much larger after 1000 °C. Microhardness was basically unchanged after the 900 °C aging, and decreased only slightly (⩽3%) after aging at 950 °C and 1000 °C.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Fusion materials and technologies · Nuclear Materials and Properties · Nuclear materials and radiation effects

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (23)

Show source-provided references
1. M.L. Hamilton, D.S. Gelles, R.J. Lobsinger, G.D. Johnson, W.F. Brown, M.M. Paxton, R.J. Puigh, C.R. Eiholzer, M.A. Blotter, Fabrication Technological Development of the Oxide Dispersion Strengthened Alloy MA957 for Fast Reactor Applications, PNNL-13168 (released 2000), 1991.10.2172/752621 ↗
2. Zakine · Mater. Sci. Eng. A · 1996 · 219 · 10210.1016/S0921-5093(96)10415-9 ↗
3. Ukai · J. Nucl. Sci. Technol. · 2002 · 39 · 87210.3327/jnst.39.872 ↗
4. Ukai · J. Nucl. Mater. · 2002 · 307–311 · 74910.1016/S0022-3115(02)01043-7 ↗
5. Alinger · J. Nucl. Mater. · 2002 · 307–311 · 48410.1016/S0022-3115(02)01220-5 ↗
6. Klueh · J. Nucl. Mater. · 2002 · 307–311 · 77310.1016/S0022-3115(02)01046-2 ↗
7. M.J. Alinger, On the Formation and Stability of Nanometer Scale Precipitates in Ferritic Alloys during Processing and High Temperature Service, PhD thesis, University of California, Santa Barbara, 2004.
8. Alamo · J. Nucl. Mater. · 2004 · 329–333 · 33310.1016/j.jnucmat.2004.05.004 ↗
9. Wilshire · Mater. Sci. Eng. A · 2004 · 386 · 8110.1016/j.msea.2004.07.047 ↗
10. Yamamoto · J. Nucl. Mater. · 2007
11. Gelles · J. Nucl. Mater. · 1996 · 233–237 · 29310.1016/S0022-3115(96)00222-X ↗
12. Alinger · J. Nucl. Mater. · 2004 · 329–333 · 38210.1016/j.jnucmat.2004.04.042 ↗
13. Yamashita · Phil. Mag. Lett. · 2004 · 84 · 52510.1080/09500830412331303609 ↗
14. Klimiankou · J. Nucl. Mater. · 2004 · 329–333 · 34710.1016/j.jnucmat.2004.04.083 ↗
15. Kishimoto · J. Nucl. Mater. · 2004 · 329–333 · 36910.1016/j.jnucmat.2004.04.044 ↗
16. M. Klimiankou, R. Lindau, A. Moslang, Micron 36 (2005) 1.10.1016/j.micron.2004.08.001 ↗
17. Miller · Intermetallics · 2005 · 133&134 · 38710.1016/j.intermet.2004.07.036 ↗
18. Miller · J. Nucl. Mater. · 2006 · 351 · 26110.1016/j.jnucmat.2006.02.004 ↗
19. Yamashita · J. Nucl. Mater. · 2002 · 307–311 · 28310.1016/S0022-3115(02)01077-2 ↗
20. Yamashita · J. Nucl. Mater. · 2004 · 329–333 · 37710.1016/j.jnucmat.2004.04.041 ↗
21. Pareige · J. Nucl. Mater. · 2007 · 360 · 13610.1016/j.jnucmat.2006.09.011 ↗
22. Miller · Microsc. Microanal. · 2004 · 10 · 70810.1017/S1431927604881169 ↗
23. Chen · Metall. Mater. Trans. A · 2002 · 33A · 271310.1007/s11661-002-0393-x ↗