Room-temperature microindentation behaviour of LWR-fuels, part 1: fuel microhardness
Source abstract
Abstract
Abstract Thorough microhardness ( H V ) measurements in LWR–UO 2 fuels in the burn-up range 40–100 GWd/t M are described. Two softening processes are found to occur in the fuels during irradiation. The first one appears at the pellet periphery when the local burn-up exceeds ≈70 GWd/t M reflecting mainly the porosity build-up after rim restructuring. The second one affects the whole fuel when it reaches on average ≈70 GWd/t M denoting a bulk irradiation damage release. The rim material is found to acquire the stiffest possible configuration of porous solids showing the lowest property drop as a function of porosity and the largest admissible porosity (≈30%) without undergoing pore-phase opening. By assimilating the hardness data to other property vs. porosity relations, it is predicted that the porous rim material would show a higher Young modulus and thermal conductivity than a low burn-up fuel at equivalent porosity. This ensures not only a stiffer but also a cooler behaviour in reactor.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Nuclear Materials and Properties · Fusion materials and technologies · Nuclear reactor physics and engineering
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (49)
Show source-provided references
1. M.R. Billaux, L.F. Van Swam, S.H. Shann, in: Proceedings of the International Topical Meeting on LWR Fuel Performance, West Palm Beach, Florida, 17–21 April 1994, p. 242
2. F. Lemoine, M. Balourdet, in: Proceedings of the International Topical Meeting on Light Water Reactor Fuel Performance, Portland, Oregon, USA, 2–6 March 1997, p. 693
3. Vollath · 1986 · Suppl. vol. C5 · 8
4. R. Manzel, M. Coquerelle, in: Proceedings of ANS International Topical Meeting on Light Water Reactor Performance, Portland, Oregon, USA, 2–6 March 1997, p. 463
5. Lawn · J. Amer. Ceram. Soc. · 1979 · 62 · 34710.1111/j.1151-2916.1979.tb19075.x ↗
6. D. Laux, G. Despaux, D. Baron, J. Spino, in: 7th International Conference on CANDU Fuel, Kingston, Ontario, Canada, 23–27 September 2001
7. Oliver · J. Mater. Res. · 1992 · 7 · 156410.1557/JMR.1992.1564 ↗
8. Spino · J. Nucl. Mater. · 1996 · 231 · 17910.1016/0022-3115(96)00374-1 ↗
9. Matzke · J. Nucl. Mater. · 1997 · 248 · 17010.1016/S0022-3115(97)00171-2 ↗
10. Rice · 1998
11. Spino · J. Nucl. Mater. · 1998 · 256 · 17910.1016/S0022-3115(98)00060-9 ↗
12. Cobos · J. Alloy Compd. · 1998 · 271–273 · 61010.1016/S0925-8388(98)00170-4 ↗
13. Spino · J. Nucl. Mater. · 2000 · 281 · 14610.1016/S0022-3115(00)00236-1 ↗
14. Manzel · J. Nucl. Mater. · 2002 · 301 · 17010.1016/S0022-3115(01)00753-X ↗
15. Tabor · 1951
16. Iost · J. Mater. Sci. · 1996 · 31 · 357310.1007/BF00360764 ↗
17. Dienst · 1969 · 82
18. J. Spino, ITU Activity Report 2001, EUR 20252, 2002, p. 54
19. J. Spino, C.T. Walker, R. Manzel, J. Nucl. Mater., in press
20. Rice · J. Amer. Ceram. Soc. · 1994 · 77 · 253910.1111/j.1151-2916.1994.tb04641.x ↗
21. Krell · J. Amer. Ceram. Soc. · 1995 · 78 · 111810.1111/j.1151-2916.1995.tb08452.x ↗
22. J.L. Bates, AEC R&D Rep. HW-77799, 1963, from [3]
23. Rice · J. Mater. Sci. · 1996 · 31 · 150910.1007/BF00357860 ↗
24. Rice · J. Mater. Sci. · 1996 · 31 · 10210.1007/BF00355133 ↗
25. Rice · Key Eng. Mater. · 1996 · 115 · 110.4028/www.scientific.net/KEM.115.1 ↗
26. Rice · J. Amer. Ceram. Soc. · 1993 · 76 · 180110.1111/j.1151-2916.1993.tb06650.x ↗
27. Rice · J. Mater. Sci. · 1997 · 32 · 473110.1023/A:1018674713006 ↗
28. Mukhopadhyay · J. Europ. Ceram. Soc. · 2000 · 20 · 2910.1016/S0955-2219(99)00092-8 ↗
29. Reynaud · J. Mater. Sci. Lett. · 2000 · 19 · 87110.1023/A:1006741616088 ↗
30. Herakovich · J. Mater. Sci. · 1999 · 34 · 159510.1023/A:1004528600213 ↗
31. Roberts · J. Amer. Ceram. Soc. · 2000 · 83 · 304110.1111/j.1151-2916.2000.tb01680.x ↗
32. Torquato · Appl. Mech. Rev. · 1991 · 44 · 3710.1115/1.3119494 ↗
33. Garboczi · Phys. Rev. E: Stat. Phys. · 1995 · 52 · 81910.1103/PhysRevE.52.819 ↗
34. D. Schrire, I. Matsson, B. Grapengiesser, in: Proceedings of the ANS International Topical Meeting on LWR Performance, Portland, Oregon, USA, 2–6 March 1997, p. 104
35. Ronchi · J. Nucl. Mater. · 1979 · 84 · 5510.1016/0022-3115(79)90150-8 ↗
36. Masche · Phys. Stat. Sol. B · 1973 · 60 · 56310.1002/pssb.2220600211 ↗
37. J. Boocock, A.S. Furzer, J.R. Matthews, AERE-M 2565, 1972, from [3]
38. Gondi · Energ. Nucl. (Milan) · 1973 · 20 · 406
39. Schulz · High Temp.–High Press. · 1981 · 13 · 649
40. P.W. Winter, D.A. MacInnes, IAEA Technical Committee Meeting on Water Reactor Fuel Element Computer Modelling in Steady-state, Transient and Accident Conditions, Preston, England, IAEA-TC-659/5.6, 1988
41. J.H. Harding, D.G. Martin, P.E. Potter, Commission of the European Communities Report EUR 12402 EN, 198910.1016/0022-3115(89)90218-3 ↗
42. INSC-Materials Property Data Base: Thermal conductivity of solid UO2. International Nuclear Safety Center, Argonne National Laboratory, USA. Assessed 1996, last modified Aug 25/99. Available from http://www.insc.anl.gov/matprop/uo2/kuo2s.html
43. Martin · J. Nucl. Mater. · 1982 · 110 · 7310.1016/0022-3115(82)90410-X ↗
44. Loeb · J. Amer. Ceram. Soc. · 1954 · 37 · 9610.1111/j.1551-2916.1954.tb20107.x ↗
45. Brandt · J. Non-Equilib. Thermodyn. · 1976 · 1 · 310.1515/jnet.1976.1.1.3 ↗
46. Maxwell · 1892
47. Bakker · J. Nucl. Mater. · 1995 · 226 · 12810.1016/0022-3115(95)00087-9 ↗
48. J.M. Gatt, Y. Monerie, D. Laux, D. Baron, J. Nucl. Mater., in press
49. Walker · J. Nucl. Mater. · 1999 · 275 · 5610.1016/S0022-3115(99)00108-7 ↗