journal article·2008-12

The transformation behaviour of the β-phase in Zr–2.5Nb pressure tubes

M. Griffiths, J.E. Winegar, A. Buyers

Journal of Nuclear Materials· Volume 383· Issue 1-2
Publisher page

Abstract

Abstract In a CANDU reactor, the fuel bundles and primary coolant are contained within Zr–2.5Nb pressure tubes that are approximately 6.3 m in length, have an internal diameter of 104 mm and a wall thickness of 4.2 mm. The Zr–2.5Nb pressure tubes are nominally extruded at 815 o C, cold-worked 27%, and stress relieved at 400 o C for 24 h, resulting in a structure consisting of elongated grains of hexagonal-close-packed α-Zr, partially surrounded by a thin network of filaments of body-centred-cubic β-Zr. These β-Zr filaments are metastable and contain about 20% Nb. The stress-relief treatment results in partial decomposition of the β-Zr filaments with the formation of hexagonal-close-packed ω-phase particles that are low in Nb, surrounded by a Nb-enriched β-Zr matrix. A temperature–time–transformation (TTT) diagram has been developed for the β-phase in Zr–2.5 wt%Nb pressure tubes. The results show that the morphology and/or physical state of the β-phase has a significant effect on the transformation behaviour compared with a bulk Zr–20 wt%Nb alloy. This means that a specific TTT-diagram is required to describe the behaviour of these engineering components.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Nuclear Materials and Properties · Titanium Alloys Microstructure and Properties · Fusion materials and technologies

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (15)

Show source-provided references
1. C.E. Lundin, R.H. Cox, USAEC Report No. 1/At(11-1)-752, 1960.
2. Aldridge · J. Nucl. Mater. · 1972 · 42 · 3210.1016/0022-3115(72)90004-9 ↗
3. Cheadle · J. Nucl. Mater. · 1973 · 47 · 25510.1016/0022-3115(73)90109-8 ↗
4. Holt · J. Nucl. Mater. · 1985 · 135 · 24610.1016/0022-3115(85)90084-4 ↗
5. Griffiths · Adv. X-ray Anal. · 1992 · 35 · 475
6. Griffiths · ASTM STP · 1993 · 1175 · 1077
7. Hehemann · Can. Met. Quart. · 1972 · 11 · 20110.1179/cmq.1972.11.1.201 ↗
8. de Fontaine · Metall. Trans. A. · 1988 · 19A · 16910.1007/BF02652523 ↗
9. Banerjee · J. Nucl. Mater. · 1976 · 62 · 22910.1016/0022-3115(76)90019-2 ↗
10. Luo · Metall. Trans. A. · 1988 · 19A · 115310.1007/BF02662575 ↗
11. Hunt · J. Nucl. Mater. · 1970 · 35 · 13410.1016/0022-3115(70)90040-1 ↗
12. Bethune · AECL-2715 · 1968
13. Abriata · Bull. Alloy Phase Diagram · 1982 · 3 · 3410.1007/BF02873409 ↗
14. Richter · J. Less Common Metals · 1962 · 4 · 25210.1016/0022-5088(62)90072-3 ↗
15. Rodgers · Trans. AIME · 1955 · 203 · 1034