TEM, XRD and nanoindentation characterization of Xenon ion irradiation damage in austenitic stainless steels

Cross-sectional and bulk specimens of a 20% cold-worked 316 austenitic stainless steel (CW 316 SS) has been characterized by TEM, XRD and nanoindentation to determine the microstructural evolution and mechanical property changes of 316 SS after irradiation with 7 MeV Xe26+ ions. TEM results reveal the presence of dislocation loops with a number density of approximately 3 x 10(22) m(-3) and sizes between 3 to 10 nm due to the collapse of vacancy rich cores inside displacement cascades. Peak broadening observed in XRD diffraction patters reveal systematic changes to lattice parameters due to irradiation. The calculated indentation values in irradiated 316 SS were found to be much higher in comparison to the unirradiated specimen, indicating the dose dependent effect of irradiation on hardness. The relationship between irradiation induced microstructural evolution and the changes to the mechanical properties of CW 316 SS are discussed in the context of fluence and irradiation temperature. (C) 2014 Elsevier B.V. All rights reserved.