Precipitation in AISI 316L(N) during creep tests at 550 and 600°C up to 10 years

A.F. Padilha, D.M. Escriba, E. Materna-Morris, M. Rieth, M. Klimenkov

Journal of Nuclear Materials· Volume 362· Issue 1
Publisher page

Abstract

The precipitation behaviour in the gauge lengths and in the heads of initially solution annealed type 316L(N) austenitic stainless steel specimens tested in creep at 550 and 600 °C for periods of up to 85 000 h has been studied using several metallographic techniques. Three phases were detected: M 23C 6 , Laves, and sigma phase. The volume fraction of the precipitated sigma phase was significantly higher than that of carbides and the Laves phase. M 23C 6 carbide precipitation occurred very rapidly and was followed by the sigma and Laves phases formation in the delta ferrite islands. Sigma and Laves phases precipitated at grain boundaries after longer times. Two different mechanisms of sigma phase precipitation have been proposed, one for delta ferrite decomposition and another for grain boundary precipitation. Small quantities of the Laves phase were detected in delta ferrite, at grain boundaries and inside the grains.
Source: expertdata · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: High Temperature Alloys and Creep · Microstructure and Mechanical Properties of Steels · Hydrogen embrittlement and corrosion behaviors in metals

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (28)

Show source-provided references
1. Treitschke · Z. Anorg. Chem. · 1907 · 55 · 40210.1002/zaac.19070550131 ↗
2. Bain · Trans. AIME · 1927 · 75 · 166
3. Jett · Met. Alloys · 1936 · 7 · 207
4. Bergmann · J. Chem. Phys. · 1951 · 19 · 51510.1063/1.1748278 ↗
5. Wiegand · Arch. Eisenhüttenwes. · 1962 · 8 · 55910.1002/srin.196203369 ↗
6. Weiss · Metall. Trans. · 1972 · 3 · 85110.1007/BF02647659 ↗
7. Minami · Mater. Sci. Technol. · 1986 · 2 · 79510.1179/mst.1986.2.8.795 ↗
8. Barcik · Mater. Sci. Technol. · 1988 · 4 · 510.1179/mst.1988.4.1.5 ↗
9. Sourmail · Mater. Sci. Technol. · 2001 · 17 · 110.1179/026708301101508972 ↗
10. Padilha · ISIJ Int. (Japan) · 2002 · 42 · 32510.2355/isijinternational.42.325 ↗
11. Rios · 2005
12. Padilha · Z. Metallkd. · 2001 · 92 · 351
13. Pohl · Z. Metallkd. · 2004 · 95 · 63110.3139/146.017999 ↗
14. Morris · Met. Sci. · 1978 · 12 · 54210.1179/msc.1978.12.11.542 ↗
15. Sasikala · J. Nucl. Mater. · 1999 · 273 · 25710.1016/S0022-3115(99)00057-4 ↗
16. Sasikala · Mater. Sci. Eng. A · 2003 · 359 · 8610.1016/S0921-5093(03)00371-X ↗
17. Sasikala · Acta Mater. · 2004 · 52 · 567710.1016/j.actamat.2004.08.029 ↗
18. Nakazawa · J. Mater. Process. Technol. · 2003 · 143–144 · 90510.1016/S0924-0136(03)00484-9 ↗
19. M. Rieth, A. Falkenstein, P. Graf, S. Reger, U. Jäntsch, M. Klimiankou, E. Materna-Morris, H. Zimmermann, Forschungszentrum Karlsruhe, Report FZKA-7065, November 2004.
20. G. Petzow, Metallographic etching, American Society for Metals (ASM), Metals Park, Ohio, USA, 1978.
21. Schumann · 2005 · vol. 14
22. Allan · Ironmak. Steelmak. · 1995 · 22 · 465
23. Padilha · ISIJ Int. (Japan) · 2003 · 43 · 13510.2355/isijinternational.43.135 ↗
24. Deighton · J. Iron Steel Inst. · 1970 · 208 · 1012
25. D.M. Escriba Villanueva, PhD thesis, University of S. Paulo, Brazil, 2005.
26. Villanueva · Mater. Sci. Technol. (London) · 2006 · 22 · 109810.1179/174328406X109230 ↗
27. Padilha · J. Nucl. Mater. · 1982 · 105 · 7710.1016/0022-3115(82)90454-8 ↗
28. Terada · J. Nucl. Mater. · 2006 · 358 · 4010.1016/j.jnucmat.2006.06.010 ↗