Microstructural development of neutron irradiated W–Re alloys

Abstract Tungsten (W) alloys are candidate materials to be used as high-heat-flux materials in fusion reactors. In our previous work, W–26 wt% Re showed drastic hardening and embrittlement after the neutron irradiation. In this study, to clarify the irradiation hardening and embrittlement behavior of W–26 wt% Re, from the viewpoint of microstructural development, the microstructure observation of the neutron irradiated W–26 wt% Re was carried out using transmission electron microscope (TEM). The specimens were irradiated at the materials open test assembly of the fast flux test facility (FFTF/MOTA-2A cycle 11) up to ∼1×10 27 n/m 2 , (En>0.1 MeV). The irradiation temperatures were 646, 679, 792, 873 and 1073 K. In all neutron irradiated W–26 wt% Re samples, sigma-phase precipitates and chi-phase precipitates were observed, while in the thermally aged specimen, only sigma-phase precipitates were observed. Irradiation effects on microstructural development are discussed.