Iron oxide waste form for stabilizing 99Tc

Crystals of goethite were synthesized with reduced technetium [{sup 99}Tc(IV)] incorporated within the solid lattice. The presence of {sup 99}Tc(IV) as a substituting cation in the matrix and 'armoring' by an additional layer of precipitated goethite isolated the reduced {sup 99}Tc(IV) from oxidizing agents. These products were used to make monolithic pellets to quantify an effective diffusion coefficient for {sup 99}Tc from goethite waste form contacted with a synthetic Hanford IDF (integrated disposal facility) pore water solution (pH = 7.2, I = 0.05 M) at room temperature for up to 120 days in static reactors. XANES analysis of the goethite solids recovered post-run demonstrated that the {sup 99}Tc in the goethite crystals remains in the reduced {sup 99}Tc(IV) state. The slow release of pertechnetate concentration with time in the static experiments with the monolith followed a square root of time dependence, consistent with diffusion control for {sup 99}Tc release. An apparent diffusion coefficient of 6.15 x 10{sup -11} cm{sup 2}/s was calculated for the {sup 99}Tc-goethite pellet sample and the corresponding leaching index (LI) was 10.2. The results of this study indicate that technetium can be immobilized in a stable, low-cost Fe oxide matrix that is easy to fabricate andmore » these findings can be useful in designing long-term solutions for nuclear waste disposal.« less