journal article·2021-05Open access

Mechanical behavior of additively manufactured and wrought 316L stainless steels before and after neutron irradiation

T.S. Byun, B.E. Garrison, M.R. McAlister, X. Chen, M.N. Gussev, T.G. Lach, A. Le Coq, K. Linton, C.B. Joslin, J.K. Carver, F.A. List, R.R. Dehoff, K.A. Terrani

Abstract

Abstract Fabrication of nuclear reactor components using additive manufacturing (AM) methods is now a practical option since the AM technologies have advanced to allow for building of complex parts with high quality materials. To assess the mechanical performance of printed components in reactor-relevant conditions and to build a property database for the AM 316L stainless steel (SS), mechanical testing and characterization were performed before and after neutron irradiation. Miniature tensile specimens were irradiated at the High Flux Isotope Reactor (HFIR) to 0.2 and 2 displacements per atom (dpa) at 300 and 600°C. The AM 316L SS was tested in the as-built, stress-relieved, and solution-annealed conditions, and the wrought (WT) 316L SS in solution-annealed condition as a reference alloy. The baseline test result showed that the AM 316L SS, regardless of the post-build heat treatment, had higher strength than the WT 316L SS, but similar ductility. Post-irradiation tensile testing was conducted at RT, 300°C, and 500°C for selected irradiation conditions. Neutron irradiation induced significant changes in the mechanical behavior of the AM stainless steels, including both hardening and softening. Although the as-built 316L steel after 300°C irradiation showed necking just after yielding, the overall property changes of the as-printed alloy became less significant after 600°C irradiation. Irradiation-induced ductilization was also observed after the higher temperature irradiation. In general, the strength change was smaller in the relatively stronger as-built and stress-relieved AM SSs than in the solution-annealed AM and WT SSs. These relatively lower strength 316L SSs overall retained higher ductility in the irradiation conditions tested, but the stronger 316L SSs demonstrated a similar level of ductility after the higher temperature (600°C) irradiation. It is a positive assessment for the AM 316L materials that no embrittlement was observed within the test and irradiation conditions of the experiment.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Additive Manufacturing Materials and Processes · Additive Manufacturing and 3D Printing Technologies · Nuclear Materials and Properties

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (48)

Show source-provided references
1. Properties of austenitic steels for nuclear reactor applications10.1016/B978-0-08-056033-5.00019-7 ↗
2. IAEA Nuclear Energy Series, NF-T-4
3. A review on the potential use of austenitic stainless steels in nuclear fusion reactors10.1007/s10894-008-9136-3 ↗
4. Assessment of austenitic stainless steels10.1016/0920-3796(95)80044-X ↗
5. Austenitic stainless steels for fast reactors -irradiation experiments, property evaluation and microstructural studies10.1016/j.egypro.2011.06.033 ↗
6. Austenitic stainless steels
7. Field · 2019
8. Simpson · 2019
9. Byun · 2020
10. Impact of defects in powder feedstock materials on microstructure of 304L and 316L stainless steel produced by additive manufacturing10.1007/s11661-018-4661-9 ↗
11. Revealing relationships between porosity, microstructure and mechanical properties of laser powder bed fusion 316L Stainless steel through heat treatment10.1016/j.matdes.2020.108481 ↗
12. Intrinsic strain aging, Σ3 boundaries, and origins of cellular substructure in additively manufactured 316L
13. Stability of cellular microstructure in laser powder bed fusion of 316L stainless steel10.1016/j.msea.2018.10.051 ↗
14. Li · 2020
15. Correlation between process parameters, microstructure and properties of 316 L stainless steel processed by selective laser melting10.1016/j.msea.2018.01.103 ↗
16. Brinkman · 1999
17. Variation of elastic mechanical properties with texture, porosity, and defect characteristics in laser powder bed fusion 316L stainless steel10.1016/j.msea.2019.138032 ↗
18. The significance of spatial length scales and solute segregation in strengthening rapid solidification microstructures of 316L stainless steel10.1016/j.actamat.2019.10.044 ↗
19. Creep behavior of 316L stainless steel manufactured by laser powder bed fusion
20. Anisotropy in the microstructure and mechanical property for the bulk and porous 316L stainless steel fabricated via selective laser melting10.1016/j.matlet.2018.09.152 ↗
21. Radiation-induced swelling and hardening of 316L stainless steel fabricated by selected laser melting10.1016/j.vacuum.2020.109183 ↗
22. Radiation damage and irradiation-assisted stress corrosion cracking of additively manufactured 316L stainless steels10.1016/j.jnucmat.2018.10.044 ↗
23. Influence of solidification structures on radiation-induced swelling in an additively-manufactured austenitic stainless steel10.1016/j.jnucmat.2019.06.012 ↗
24. Ferritic-austenitic solidification mode in austenitic stainless steel welds10.1007/BF02661201 ↗
25. Champlin · 2019
26. HFIR irradiation testing supporting the transformational challenge reactor
27. Tensile properties of candidate SNS target container materials after proton and neutron irradiation in the LANSCE accelerator10.1016/S0022-3115(01)00515-3 ↗
28. 2016
29. 2020
30. Additively manufactured hierarchical stainless steels with high strength and ductility10.1038/nmat5021 ↗
31. Evolution of cellular dislocation structures and defects in additively manufactured austenitic stainless steel under ion irradiation10.1016/j.scriptamat.2019.11.036 ↗
32. Intragranular cellular segregation network structure strengthening 316L stainless steel prepared by selective laser melting10.1016/j.jnucmat.2015.12.034 ↗
33. Evolution of cellular dislocation structures and defects in additively manufactured austenitic stainless steel under ion irradiation10.1016/j.scriptamat.2019.11.036 ↗
34. Antoun · 2018
35. High temperature plastic instability and dynamic strain aging in the tensile behavior of AISI 316 stainless steel10.1590/1980-5373-mr-2016-0854 ↗
36. A statistical distribution function of wide applicability10.1115/1.4010337 ↗
37. Weibull distribution analysis of the tensile strength of the Kenaf Bast fiber10.1007/s12221-016-6176-6 ↗
38. Statistical model for carbide induced brittle fracture in steel10.1179/030634584790420384 ↗
39. Characterization of tensile strength and fracture toughness of nuclear graphite NBG-18 using subsize specimens10.1016/j.jnucmat.2011.03.019 ↗
40. Stacking fault energies of seven commercial austenitic stainless steels10.1007/BF02641927 ↗
41. Formation of shear bands and strain-induced martensite during plastic deformation of metastable austenitic stainless steels10.1016/j.actamat.2007.07.015 ↗
42. On the stress dependence of partial dislocation separation and deformation microstructure in austenitic stainless steels10.1016/S1359-6454(03)00117-4 ↗
43. Temperature dependence of strain hardening and plastic instability behaviors in austenitic stainless steels10.1016/j.actamat.2004.05.003 ↗
44. Deformation mode map of irradiated 316 stainless steel in true stress-dose space10.1016/j.jnucmat.2006.02.033 ↗
45. Effects of dynamic strain aging on strain hardening behavior, dislocation substructure, and fracture morphology in a ferritic stainless steel10.1007/s11661-019-05574-6 ↗
46. Evolution of fine-scale defects in stainless steels neutron-irradiated at 275 C10.1016/S0022-3115(03)00002-3 ↗
47. Radiation embrittlement behavior of fine-grained molybdenum alloy with 0.2 wt¾TiC addition10.1016/j.jnucmat.2005.06.013 ↗
48. Ductilization of TiAl intermetallic alloys by neutron-irradiation10.1016/0966-9795(95)00030-5 ↗