Enhanced thermal conductivity of uranium dioxide–silicon carbide composite fuel pellets prepared by Spark Plasma Sintering (SPS)
Source abstract
Abstract
Abstract Uranium dioxide (UO2)–10 vol% silicon carbide (SiC) composite fuel pellets were produced by oxidative sintering and Spark Plasma Sintering (SPS) at a range of temperatures from 1400 to 1600 °C. Both SiC whiskers and SiC powder particles were utilized. Oxidative sintering was employed over 4 h and the SPS sintering was employed only for 5 min at the highest hold temperature. It was noted that composite pellets sintered by SPS process revealed smaller grain size, reduced formation of chemical products, higher density, and enhanced interfacial contact compared to the pellets made by oxidative sintering. For given volume of SiC, the pellets with powder particles yielded a smaller grain size than pellets with SiC whiskers. Finally thermal conductivity measurements at 100 °C, 500 °C, and 900 °C revealed that SPS sintered UO2–SiC composites exhibited an increase of up to 62% in thermal conductivity compared to UO2 pellets, while the oxidative sintered composite pellets revealed significantly inferior thermal conductivity values. The current study points to the improved processing capabilities of SPS compared to oxidative sintering of UO2–SiC composites.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Nuclear Materials and Properties · Advanced ceramic materials synthesis · Nuclear materials and radiation effects
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (29)
Show source-provided references
1. Amaya · J. Nucl. Mater. · 2002 · 300 · 5710.1016/S0022-3115(01)00704-8 ↗
2. Krishna · Nucl. Eng. Des. · 1981 · 65 · 28310.1016/0029-5493(81)90094-7 ↗
3. Khan · Nucl. Technol. · 2010 · 169 · 6110.13182/NT10-A9343 ↗
4. Verrall · J. Nucl. Mater. · 1999 · 274 · 5410.1016/S0022-3115(99)00089-6 ↗
5. Hickman · Stud. Radiat. Eff. Solids · 1966 · 1 · 72
6. Hunt · J. Nucl. Mater. · 2012 · 427 · 24510.1016/j.jnucmat.2012.04.027 ↗
7. G.C. Allen, J.A. Crofts, T. Swan, in: Proceedings of the 7th. International Symposium on the Reactivity of Solids, 1972, pp. S4/1–S4/10.
8. Solomon · 2006
9. Sarma · J. Nucl. Mater. · 2006 · 352 · 32410.1016/j.jnucmat.2006.02.090 ↗
10. Latta · Heat Transfer Eng. · 2008 · 29 · 35710.1080/01457630701825390 ↗
11. J. Wang, Developing a high thermal conductivity nuclear fuel with silicon carbide additives, Ph.D. Dissertation, University of Florida, 2008.
12. Assmann · J. Nucl. Mater. · 1986 · 140 · 110.1016/0022-3115(86)90189-3 ↗
13. Williams · J. Nucl. Mater. · 1959 · 1 · 2810.1016/0022-3115(59)90008-X ↗
14. Dehaudt · J. Nucl. Mater. · 2001 · 299 · 25010.1016/S0022-3115(01)00661-4 ↗
15. Chevrel · J. Nucl. Mater. · 1992 · 189 · 17510.1016/0022-3115(92)90530-X ↗
16. Shen · Nanotechnology · 2006 · 17 · 218710.1088/0957-4484/17/9/018 ↗
17. Zhang · Chem. Phys. Lett. · 2011 · 510 · 10910.1016/j.cplett.2011.05.013 ↗
18. Cheng · J. Mater. Sci. Technol. · 2011 · 27 · 116510.1016/S1005-0302(12)60013-9 ↗
19. Munir · J. Mater. Sci. · 2006 · 41 · 76310.1007/s10853-006-6555-2 ↗
20. Omori · Mater. Sci. Eng., A · 2000 · 287 · 18310.1016/S0921-5093(00)00773-5 ↗
21. Zhijian · J. Am. Ceram. Soc. · 2002 · 85 · 192110.1111/j.1151-2916.2002.tb00381.x ↗
22. Dollimore · Surf. Technol. · 1976 · 4 · 12110.1016/0376-4583(76)90024-8 ↗
23. Willis · Scripta Metall. · 1987 · 21 · 173310.1016/0036-9748(87)90167-0 ↗
24. Fink · J. Nucl. Mater. · 2000 · 279 · 110.1016/S0022-3115(99)00273-1 ↗
25. Mingo · Phys. Rev. B · 2006 · 74 · 1210.1103/PhysRevB.74.125402 ↗
26. Ramana · ACS Appl. Mater. Inter. · 2011 · 4 · 20010.1021/am2012596 ↗
27. Soyez · Appl. Phys. Lett. · 2000 · 77 · 115510.1063/1.1289803 ↗
28. Youngblood · J. Nucl. Mater. · 2004 · 329–333 · 50710.1016/j.jnucmat.2004.04.111 ↗
29. Maruyama · J. Nucl. Mater. · 2004 · 329–333 · 102210.1016/j.jnucmat.2004.04.128 ↗