Air oxidation of Zircaloy-4, M5® and ZIRLO™ cladding alloys at high temperatures
Source abstract
Abstract
Abstract The paper presents the results of isothermal and transient oxidation experiments of the advanced cladding alloys M5® and ZIRLO™ in comparison to Zircaloy-4 in air at temperatures from 973 to 1853 K. Generally, oxidation in air leads to a strong degradation of the cladding material. The main mechanism of this process is the formation of zirconium nitride and its re-oxidation. From the point of view of safety, the barrier effect of the fuel cladding is lost much earlier than during accident transients with a steam atmosphere only. Comparison of the three alloys investigated reveals a qualitatively similar, but quantitatively varying oxidation behavior in air. The mainly parabolic oxidation kinetics, where applicable, is comparable for the three alloys. Strong differences of up to 500% in oxidation rates were observed after transition to linear kinetics at temperatures below 1300 K. The paper presents kinetic rate constants as well as critical times and oxide scale thicknesses at the point of transition from parabolic to linear kinetics.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Nuclear Materials and Properties · Nuclear reactor physics and engineering · High-Temperature Coating Behaviors
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (18)
Show source-provided references
1. Cox · J. Nucl. Mater. · 2005 · 336 · 33110.1016/j.jnucmat.2004.09.029 ↗
2. Schanz · Nucl. Eng. Design · 2004 · 232 · 7510.1016/j.nucengdes.2004.02.013 ↗
3. D.A. Powers, L.N. Kmetyk, R.C. Schmidt, A Review of Technical Issues of Air Ingression during Severe Reactor Accidents, Report NUREG/CR-6218, SAND94-0731, Sandia National Lab., 1994.
4. I. Shepherd et al., Oxidation Phenomena in Severe Accidents (OPSA), Final Report, INV-OPSA(99)-P008, 2000.
5. Shepherd · Nucl. Eng. Design · 2001 · 209 · 10710.1016/S0029-5493(01)00393-4 ↗
6. Natesan · 2004
7. P. Giordano, C. Séropian, The Air Ingress Issue for PWRs, in: 5th Technical Seminar on the Phebus FP Programme, Aix-en-Provence, June 2003.
8. Duriez · J. Nucl. Mater. · 2008 · 380 · 3010.1016/j.jnucmat.2008.07.002 ↗
9. Steinbrück · J. Nucl. Mater. · 2009 · 392 · 53110.1016/j.jnucmat.2009.04.018 ↗
10. Hózer · Nucl. Technol. · 2003 · 141 · 24410.13182/NT03-A3365 ↗
11. A. Kiselev et al., The main results and conclusions of the VVER fuel assemblies tests under severe accident conditions in the large-scale PARAMETER facility, in: Proc. of the 16th Int. QUENCH Workshop, 16–18.11.2010, Karlsruhe, Germany, ISBN 978-3-923704-74-3.
12. Steinbrück · Nucl. Eng. Design · 2006 · 236 · 170910.1016/j.nucengdes.2006.04.010 ↗
13. G. Schanz, et al., Results of the QUENCH-10 Experiment on Air Ingress, Forschungszentrum Karlsruhe, FZKA 7087, 2006.
14. M. Steinbrück, U. Stegmaier, T. Ziegler, Prototypical Experiments on Air Oxidation of Zircaloy-4 at High Temperatures, Forschungszentrum Karlsruhe, FZKA 7257, 2007.
15. M. Steinbrück, N. Vér, M. Große, Oxidation of advanced zirconium cladding alloys in steam at temperatures 600–1200°C, Oxid. Met., in press. doi:10.1007/s11085-011-9249-3.10.1007/s11085-011-9249-3 ↗
16. M. Steinbrück, N. Vér, High-temperature oxidation of Zircaloy-4 in mixed steam-air and steam-nitrogen atmospheres, in: Proc. ICAPP’10, Paper 10168, San Diego, CA, USA, 13–17 June 2010.
17. J.V. Cathcart, et al., Zirconium Metal–Water Oxidation Kinetics, IV: Reaction Rate Studies, Report ORNL/NUREG-17, 1977.10.2172/7317596 ↗
18. Steinbrück · Oxid. Met. · 2008 · 70 · 31710.1007/s11085-008-9124-z ↗