Isolating the effect of radiation-induced segregation in irradiation-assisted stress corrosion cracking of austenitic stainless steels

Post-irradiation annealing was used to help identify the role of radiation-induced segregation (RIS) in irradiation-assisted stress corrosion cracking (IASCC) by preferentially removing dislocation loop damage from proton-irradiated austenitic stainless steels while leaving the RIS of major and minor alloying elements largely unchanged. The goal of this study is to better understand the underlying mechanisms of IASCC. Simulations of post-irradiation annealing of RIS and dislocation loop microstructure predicted that dislocation loops would be removed preferentially over RIS due to both thermodynamic and kinetic considerations. To verify the simulation predictions, a series of post-irradiation annealing experiments were performed. Both a high purity 304L (HP-304L) and a commercial purity 304 (CP-304) stainless steel alloy were irradiated with 3.2 MeV protons at 360 °C to doses of 1.0 and 2.5 dpa. Following irradiation, post-irradiation anneals were performed at temperatures ranging from 400 to 650 °C for times between 45 and 90 min. Grain boundary composition was measured using scanning transmission electron microscopy with energy-dispersive spectrometry in both as-irradiated and annealed samples. The dislocation loop population and radiation-induced hardness were also measured in as-irradiated and annealed specimens. At all annealing temperatures above 500 °C, the hardness and dislocation densities decreased with increasing annealing time or temperature much faster than RIS. Annealing at 600 °C for 90 min removed virtually all dislocation loops while leaving RIS virtually unchanged. Cracking susceptibility in the CP-304 alloy was mitigated rapidly during post-irradiation annealing, faster than RIS, dislocation loop density or hardening. That the cracking susceptibility changed while the grain boundary chromium composition remained essentially unchanged indicates that Cr depletion is not the primary determinator for IASCC susceptibility. For the same reason, the visible dislocation microstructure and radiation-induced hardening are also not sufficient to cause IASCC alone.