Mechanical properties of irradiated ODS-EUROFER and nanocluster strengthened 14YWT
Source abstract
Abstract
Irradiations to 1.5 dpa at 300–750 °C were conducted to investigate the changes in mechanical properties of an advanced nanocluster strengthened ferritic alloy, designated 14YWT, and an oxide dispersion strengthened ferritic alloy ODS-EUROFER. Two non-dispersion strengthened variants, 14WT and EUROFER 97, were also irradiated and tested. Tensile results show 14YWT has very high tensile strengths and experienced some radiation-induced hardening, with an increase in room temperature yield strength of 125 MPa after irradiation, while results for ODS-EUROFER show a 275 MPa increase following irradiation. Master curve fracture toughness analysis show 14YWT has a cryogenic T o reference temperatures before and after irradiation of about −188 and −176 °C, respectively, and upper-shelf K J Ic values between 175 and 225 MPa√m. The favorable fracture toughness properties and resistance to radiation-induced changes in mechanical properties observed for 14YWT are attributed to a fine grain structure and high number density of Y–Ti–O nanoclusters.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Fusion materials and technologies · Nuclear Materials and Properties · Nuclear materials and radiation effects
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (22)
Show source-provided references
1. Huet · Powder Metall. · 1967 · 10 · 20810.1179/pom.1967.10.20.010 ↗
2. Huet · Nucl. Technol. · 1974 · 24 · 21610.13182/NT74-A31476 ↗
3. van der Schaaf · Fusion Eng. Des. · 2003 · 69 · 19710.1016/S0920-3796(03)00337-5 ↗
4. Lindau · J. Nucl. Mater. · 2002 · 307–311 · 76910.1016/S0022-3115(02)01045-0 ↗
5. Lindau · Fusion Eng. Des. · 2005 · 75–79 · 98910.1016/j.fusengdes.2005.06.186 ↗
6. de Castro · J. Nucl. Mater. · 2007 · 367–370 · 19610.1016/j.jnucmat.2007.03.146 ↗
7. Klimiankou · J. Nucl. Mater. · 2007 · 367–370 · 17310.1016/j.jnucmat.2007.03.150 ↗
8. Larson · Scripta Mater. · 2001 · 44 · 35910.1016/S1359-6462(00)00593-5 ↗
9. Miller · Mater. Sci. Eng. A · 2003 · A353 · 14010.1016/S0921-5093(02)00680-9 ↗
10. Miller · Intermetallics · 2005 · 13 · 38710.1016/j.intermet.2004.07.036 ↗
11. Klueh · J. Nucl. Mater. · 2002 · 307–311 · 77310.1016/S0022-3115(02)01046-2 ↗
12. Yamamoto · J. Nucl. Mater. · 2007 · 367–370 · 39910.1016/j.jnucmat.2007.03.047 ↗
13. Pareige · J. Nucl. Mater. · 2007 · 360 · 13610.1016/j.jnucmat.2006.09.011 ↗
14. Sokolov · J. Nucl. Mater. · 2007 · 367–370 · 21310.1016/j.jnucmat.2007.03.143 ↗
15. McClintock · J. Nucl. Mater. · 2009 · 386–388 · 30710.1016/j.jnucmat.2008.12.104 ↗
16. Alinger · J. Nucl. Mater. · 2004 · 329–333 · 38210.1016/j.jnucmat.2004.04.042 ↗
17. L.L. Snead (principal developer of the SiC temperature monitor technique for HFIR rabbit capsule irradiations at Oak Ridge National Laboratory): private communication 2006.
18. Miller · J. Nucl. Mater. · 2006 · 351 · 26110.1016/j.jnucmat.2006.02.004 ↗
19. J.J. Fischer, U.S. Patent 4,075,010, Dispersion Strengthened Ferritic Alloy for use in Liquid Metal Fast Breeder Reactors, February 21, 1978.
20. Miller · J. Nucl. Mater. · 2004 · 329–333 · 33810.1016/j.jnucmat.2004.04.085 ↗
21. Alinger · J. Nucl. Mater. · 2002 · 307–311 · 48410.1016/S0022-3115(02)01220-5 ↗
22. Fu · Phys. Rev. Lett. · 2007 · 99 · 225502-1