Surface properties of tannin‐impregnated and varnished beech wood after exposure to accelerated weathering
Source abstract
Abstract
The aim of this study was to determine selected surface properties of varnished beech wood impregnated with natural extracts after exposure to accelerated weathering. Beech wood samples were impregnated with aqueous solutions of 5 and 10% mimosa (Acacia mollissima) and quebracho (Shinopsis lorentzii) tannins. After weathering, colour changes (ΔL*, Δa*, Δb*, and ΔE*) in addition to scratch resistance and surface hardness values were calculated and evaluated. As a result of the weathering process, greater colour changes (ΔE*) were detected in the beech wood samples impregnated with tannins compared with the unimpregnated control samples. The least colour change occurred in the Tanalith‐E‐impregnated samples. Total colour change was adversely affected with tannin impregnation after the weathering processes. In terms of surface hardness and scratch resistance, the highest values were observed in the mimosa‐solution‐impregnated and control samples. Furthermore, it was found that scratch resistance and hardness values tended to increase during the first period of weathering and decreased thereafter. Regarding surface properties, the best results were obtained when polyurethane varnish was employed compared with the other varnish types.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Wood Treatment and Properties · Lignin and Wood Chemistry · Cultural Heritage Materials Analysis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Forest Products Engineering Faculty of Forestry Duzce University 81620 Duzce Turkey
Department of Wood Products Industrial Engineering Faculty of Technology Duzce University 81620 Duzce Turkey
Funding
Directory of Scientific Research Projects of Duzce University
References (41)
Show source-provided references
1. 10.1016/S0300-9440(03)00102-410.1016/S0300-9440(03)00102-4 ↗
2. 10.1155/2015/52657010.1155/2015/526570 ↗
3. 10.1016/S0031-9422(02)00267-410.1016/S0031-9422(02)00267-4 ↗
4. 10.1007/s11998-004-0015-110.1007/s11998-004-0015-1 ↗
5. 10.1016/j.polymdegradstab.2012.01.01310.1016/j.polymdegradstab.2012.01.013 ↗
6. 10.1111/cote.1207010.1111/cote.12070 ↗
7. Williams R S · 2005
8. Ghosh S C · BioResources · 2009 · 4 · 65910.15376/biores.4.2.659-673 ↗
9. 10.1016/j.conbuildmat.2015.07.04910.1016/j.conbuildmat.2015.07.049 ↗
10. 10.1016/j.ibiod.2015.10.01010.1016/j.ibiod.2015.10.010 ↗
11. 10.1016/j.ibiod.2013.06.00410.1016/j.ibiod.2013.06.004 ↗
12. 10.1007/BF0053896110.1007/BF00538961 ↗
13. 10.1016/j.porgcoat.2010.08.00610.1016/j.porgcoat.2010.08.006 ↗
14. 10.1016/j.indcrop.2009.10.01010.1016/j.indcrop.2009.10.010 ↗
15. ASTM D 3023‐81 Determination of resistance of factory applied coatings on wood products of stain and reagents(West Conshohocken PA:ASTM 1981).
16. ISO 4892‐3 Plastics: Methods of exposure to laboratory light sources. Part 3: Fluorescent UV lamps(Basel:ISO 2013).
17. BS EN 15186:2012 Furniture: Assessment of the surface resistance to scratching(London:BSI 2012).
18. ISO 1522:1998 Paints and varnishes. Pendulum damping test(Basel:ISO 1998).
19. ASonmez Durability of varnishes used on surfaces of wooden furniture against important physical mechanical and chemical effects(Ankara:Gazi University 1989).
20. ASTM D 2244‐3:2007 Standard practice for calculation of color tolerances and color differences from instrumentally measured color coordinates(West Conshohocken PA:ASTM 2007).
21. 10.15376/biores.7.4.5138-515110.15376/biores.7.4.5138-5151 ↗
22. Feist W C · Am. Chem. Soc. · 1984 · 401
23. Budakci M · J. For. Fac. · 2014 · 14 · 37
24. MAtar The effects of bleaching chemicals on the finishing processes of wood materials(Ankara:Gazi University 1999).
25. Grelier S · Wood Fiber Sci. · 2000 · 32 · 196
26. 10.15376/biores.7.4.4875-488810.15376/biores.7.4.4875-4888 ↗
27. DSoylamis The effect of some water repellent impregnated materials on the covering surface applications(Zonguldak:Zonguldak Karaelmas University 2007).
28. Budakci M · Afr. J. Biotechnol. · 2010 · 9 · 3595
29. MBudakci Design and production of a new adhesion testing device and its utilization with testing of wood varnishes(Ankara:Gazi University 2003).
30. Ozgenc O · J. For. Fac. · 2013 · 14 · 203
31. JZhangandP DKamdem Int. Res. Group Wood Preserv. Conf. Kona HI(2000) IRG/WP/00‐40155.
32. 10.1016/S0141-3910(02)00026-510.1016/S0141-3910(02)00026-5 ↗
33. 10.1016/j.apsusc.2006.08.02910.1016/j.apsusc.2006.08.029 ↗
34. 10.1016/j.apsusc.2006.12.00510.1016/j.apsusc.2006.12.005 ↗
35. NCakicier Changes due to weathering of surface finishing layers of wood(Istanbul:Istanbul University 2007).
36. UAyata Determination of the resistance of water based layers on some heat treated (Thermowood) wood species against accelerated UV aging(Duzce:Duzce University 2014).
37. HPeker Efficiency of treatment chemical materials to varnishes used on surfaces of furniture(Trabzon:Karadeniz Technical University 1997).
38. MYakin Effects of the resistance to adhesion glossy and hardness at the waterborne varnishes(Ankara:Gazi University 2001).
39. Sonmez A · J. Polytechnic · 2004 · 7 · 229
40. IKesik The layer performance of water based varnishes on wood preprocessed with various chemicals(Ankara:Gazi University 2009).
41. 10.1016/S0141-3910(03)00276-310.1016/S0141-3910(03)00276-3 ↗