Fabrication of surface crystallized glasses with α-Zn3B2O6 and their optical property

Abstract Surface crystallization of metastable α-Zn 3 B 2 O 6 was observed in ZnO-B 2 O 3 -CaO-K 2 O-Al 2 O 3 glass after conventional heat treatment. Precipitation of α-Zn 3 B 2 O 6 with high orientation degree in the transparent glass–ceramics was confirmed by XRD measurement. Transmission electron microscope image showed that crystalline rods of α-Zn 3 B 2 O 6 were precipitated from the surface of the glass–ceramics with the crystalline orientation of (1 − 2 1) direction. Although the strongly oriented phase was observed in the glass–ceramics, the polarization direction was not strong from the crystal that can bring strong second harmonic generation (SHG). SHG measurement using a powder sample showed that the 2nd optical nonlinearity of α-Zn 3 B 2 O 6 glass–ceramics was comparable to that of α-SiO 2 .