Nuclear magnetic resonance studies of aluminosilicate gels prepared in high-alkaline and salt-concentrated solutions

Abstract Solid-state 29 Si, 27 Al, and 23 Na magic angle spinning (MAS) NMR techniques in combination with X-ray powder diffraction (XRD) are used to characterize aluminosilicate gels as a function of composition, pH, and reaction times. These gels were prepared at 80 °C using initial solutions with low Si/Al ratios, high alkaline and salt concentrations that are characteristic of nuclear tank wastes. XRD data show that cancrinite and sodalite are the main crystalline phases in the aluminosilicate gels produced. It is found that the pH and the salt content have significant effects on the nature of the aluminosilicate gels. Higher pH appears to increase the rate of crystallization, the degree of overall crystallinity and the percentage of cancrinite phases in aluminosilicate gels, whereas the high-salt concentration promotes the formation of cancrinite and sodalite and prohibits the formation of other zeolites. Complementary to XRD, NMR is extremely useful for providing the information on the structure of amorphous intermediate gels with no long-range order.