Structural and thermal properties of Se85S15−xSbx glassy system

Abstract Bulk glasses of Se 85 S 15− x Sb x system, where x =0,3,6,9,12, and 15 at.%, were prepared and investigated by X-ray diffraction, differential scanning calorimetry (DSC) and ultrasonic techniques. The results reveal that the glass transition temperature T g , the crystallisation temperature, T c and the melting temperature, T m , appeared in the temperature range 300–490 K and are strongly affected by the Sb content. However, all transition temperature peaks observed on both DSC thermograms and ultrasonic attenuation spectra were assigned according to previous data on chalcogenides. The present investigations indicate that the prepared system is structurally inhomogeneous at a molecular level, in which Se–S, Se 3 Sb 2 phases are dispersed in an Se–Se matrix.