Improvement of the chemical resistance of zirconium fluoride glasses coated with a Tiron® modified tin oxide layer prepared by the sol–gel process

Abstract In order to improve the chemical resistance of zirconium fluoride glass a protective transparent SnO 2 layer was deposited by the sol–gel dip-coating process in the presence of Tiron ® as particle surface modifier agent. After water immersion for different periods of time, both coated and non-coated fluoride glasses were analyzed by scanning electron microscopy, mass loss evaluation, infrared spectroscopy and X-ray photoelectron spectroscopy. In contrast to the effects occurring for non-coated glass, where the surface undergoes a rapid selective dissolution of the most soluble species, the results for the SnO 2 -coated glass showed that the filling of the film nanopores by dissolved glass material results in a hermetic barrier protecting the glass surface. The selective glass dissolution was confirmed by liquid chromatography measurements of the etching solution after each exposure time.