Glass formation and short-range order structures in the BaS + La2S3 + GeS2 system

Josh R. Roth, Steve W. Martin, John Ballato, Hong A. Qiao, Norman C. Anheier

Abstract

Abstract Infrared (IR) optical materials have enabled a broad range of optical sensing and measurement applications in the mid-wave and long-wave IR. Many IR transmitting glasses are based on covalently-bonded selenides and tellurides, such as As2Se3 and GeTe2, which typically have relatively low glass transition temperatures (Tg) on the order of 200 to 350 °C. Many applications have working temperatures above the Tg of these materials, which compels the development of new IR materials. This work studies the underlying short-range order (SRO) structure and glass formability of a new family of ionically-bonded sulfide glasses, xBaS + yLa2S3 + (1 − x − y)GeS2, to develop high Tg optical materials with a broad IR transmission range. These sulfide glasses were produced by melting sulfide materials inside evacuated and sealed carbon-coated silica ampoules at 1150 °C for 12 h and quenching to room temperature to form glass. Glass samples were then characterized by IR and Raman spectroscopies and differential thermal analysis (DTA). It was found that by increasing the modifier concentration, the predominantly Ge4 SRO units, the superscript defines the number of bridging sulfur (BS) ions in the tetrahedral network found in GeS2 glasses, are ultimately converted to Ge0 units at >40 mol% network modifier content through the generation of non-bridging sulfur (NBS) ions. These molecular ionic units still form a glassy network, with some of the highest reported Tg values to date for a pure sulfide glass. This suggests that this composition has strong ionic bonds between negatively-charged tetrahedral SRO units and the positively-charged modifier cations. While the glass network is depolymerized in the high modifier content glasses though the formation of a high concentration of molecular ionic Ge0 SRO groups, they are, nevertheless, homogeneous glassy materials that exhibit the largest Tg and ΔT (difference between crystallization temperature, Tc, and Tg) values of glasses in this system, making them the optimal glasses for high Tg IR optical components, including, potentially, refractory IR optical fibers.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Phase-change materials and chalcogenides · Glass properties and applications · Luminescence Properties of Advanced Materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (40)

Show source-provided references
1. E.I. Administration · 2017
2. Greene · 2011
3. Annual report 2011, Gen IV international forum
4. Infrared laser-absorption sensing for combustion gases10.1016/j.pecs.2016.12.002 ↗
5. Chalcogenide glasses: a review of their preparation, properties and applications10.1016/0022-3093(94)00686-5 ↗
6. Chalcogenide glass fibers: optical window tailoring and suitability for bio-chemical sensing10.1016/j.optmat.2015.06.034 ↗
7. Purification of Te75Ga10Ge15 glass for far infrared transmitting optics for space application10.1016/j.optmat.2010.02.030 ↗
8. From selenium- to tellurium-based glass optical fibers for infrared spectroscopies10.3390/molecules18055373 ↗
9. IR, Raman, and NMR studies of the short-range structures of 0.5Na2S + 0.5[xGeS2 + (1 − x)PS5/2] mixed glass-former glasses10.1021/jp4111053 ↗
10. Structure and properties of glasses in the MI + M2S + (0.1Ga2S3 + 0.9GeS2), M = Li, Na, K and Cs, system10.1016/j.jnoncrysol.2007.11.006 ↗
11. The glass transition temperature of mixed glass former 0.35Na2O + 0.65[xB2O3 + (1 − x)P2O5] glasses10.1016/j.jnoncrysol.2011.12.068 ↗
12. The densities of mixed glass former 0.35 Na2O + 0.65 [xB2O3 + (1 − x)P2O5] glasses related to the atomic fractions and volumes of short range structures10.1016/j.jnoncrysol.2011.10.018 ↗
13. Structural studies of mixed glass former 0.35Na2O + 0.65[xB2O3 + (1 − x)P2O5] glasses by Raman and 11B and 31P magic angle spinning nuclear magnetic resonance spectroscopies10.1021/jp308494a ↗
14. Modulated-temperature differential scanning calorimetry and Raman spectroscopy studies of AsxS100 − x glasses10.1023/A:1004455929749 ↗
15. Structure and properties of As2S3 and As2Se3 glasses modified with Dy, Sm and Mn
16. Optical properties and applications of chalcogenide glasses: a review10.1016/j.jnoncrysol.2003.08.064 ↗
17. Laboratory preparation of highly pure As2Se3 glass10.1016/S0022-3093(94)00512-5 ↗
18. Glass formation in the GexTe100 − x binary system: synthesis by twin roller quenching and co-thermal evaporation techniques10.1016/j.jnoncrysol.2009.04.072 ↗
19. Chemical aspects of glass formation in telluride systems10.1016/0022-3093(72)90121-4 ↗
20. Detecting bacteria contamination on medical device surfaces using an integrated fiber-optic mid-infrared spectroscopy sensing method10.1016/j.snb.2016.03.044 ↗
21. Infrared-transparent glass ceramics: an exploratory study10.1016/j.jnoncrysol.2014.11.040 ↗
22. Thermal properties of Ga2S3-based glass and their consideration during fiber drawing10.1016/S0022-3093(99)00540-2 ↗
23. Microstructure and thermal-stability of amorphous materials in the GES2-LA2S3 system10.1557/JMR.1991.2694 ↗
24. New sulfide and selenide glasses: preparation, structure, and properties10.1111/j.1151-2916.1968.tb15675.x ↗
25. Oxygen-excess-related point defects in glassy/amorphous SiO2 and related materials10.1016/j.nimb.2012.02.038 ↗
26. Response of commercial window glass to gamma doses10.1016/j.physb.2007.09.074 ↗
27. Color centers of a borosilicate glass induced by 10 MeV proton, 1.85 MeV electron and 60Co-γ ray10.1016/j.radphyschem.2013.01.044 ↗
28. Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides10.1107/S0567739476001551 ↗
29. Structure and optical conductivity of silver thiogermanate glasses10.1006/jssc.1994.1301 ↗
30. Raman scattering in GeS2 glass and its crystalline polymorphs compared10.1016/S0022-2860(97)00184-1 ↗
31. Glass formation, structure and ionic conduction in the sodium sulfide-germanium sulfide (Na2S-GeS2) system10.1016/0022-3093(80)90473-1 ↗
32. Chalcogenide glass of the GeS2 system. Glass formation range
33. The comparative structure, properties, and ionic conductivity of LiI + Li2S + GeS2 glasses doped with Ga2S3 and La2S310.1016/j.jnoncrysol.2007.08.058 ↗
34. Microstructure and thermal stability of amorphous materials in the germanium sulfide-lanthanum sulfide (GeS2-La2S3) system10.1557/JMR.1991.2694 ↗
35. Novel glasses in rare-earth sulfide systems
36. Raman spectroscopic analysis on the solubility mechanism of La3+ in GeS2–Ga2S3 glasses10.1016/S0022-3093(98)00577-8 ↗
37. Polysulfide anions. 1. Structure and vibrational spectra of the S22- and S32- anions. Influence of the cations on bond length and angle10.1021/ic9811143 ↗
38. Sol–gel derived germanium sulfide planar waveguides10.1016/S1369-8001(00)00053-6 ↗
39. The comparative structure, properties, and ionic conductivity of LiI + Li2S + GeS2 glasses doped with Ga2S3 and La2S310.1016/j.jnoncrysol.2007.08.058 ↗
40. Preparation and characterization of germanium oxy-sulfide GeS2–GeO2 glasses10.1016/j.jnoncrysol.2005.05.020 ↗