Phase separation and sample size independence of fracture strength for (Mg0.585Cu0.305Y0.11)95Be5 bulk metallic glass

L. Wang, K.Q. Qiu, J.H. You, Y.L. Ren, R.D. Li

Publisher page

Abstract

Abstract An (Mg 0.585 Cu 0.305 Y 0.11 ) 95 Be 5 bulk metallic glass (BMG) with high strength was fabricated by conventional Cu-mold casting method. The phase structure, thermal stability and microstructure of the BMG were investigated by using X-ray diffraction, differential scanning calorimetry, transmission electron microscopy and scanning electron microscopy. The results show that the quaternary (Mg 0.585 Cu 0.305 Y 0.11 ) 95 Be 5 BMG with 3 mm in diameter exhibits obvious glass transition T g of 429 K and a wide supercooled liquid region Δ T x of 53 K. Meanwhile, the phase-separated regions characteristic of Cu–Y–Be glass containing nanometer CuY crystals are heterogeneously distributed in the Mg–Cu–Y glassy matrix in the as-cast samples. Under uniaxial compressive loading, the samples with 1, 2 and 3 mm in diameter show high strength up to 959, 955 MPa and 954 MPa, respectively. The sample-size independence of fracture strength was for the first time found in the Mg-TM–RE metallic glasses. The effects of Be addition on phase separation and mechanical properties for Mg–Cu–Y alloy system were discussed.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Metallic Glasses and Amorphous Alloys · Electromagnetic wave absorption materials · Magnetic Properties of Alloys

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (30)

Show source-provided references
1. Wang · Mater. Sci. Eng. R · 2004 · 44 · 4510.1016/j.mser.2004.03.001 ↗
2. Inoue · Acta Mater. · 2000 · 48 · 27910.1016/S1359-6454(99)00300-6 ↗
3. Johnson · MRS Bull. · 1999 · 24 · 4210.1557/S0883769400053252 ↗
4. Li · Mater. Sci. Eng., A · 2008 · 491 · 42010.1016/j.msea.2008.04.036 ↗
5. Ma · Appl. Phys. Lett. · 2003 · 83 · 279310.1063/1.1616192 ↗
6. Hui · Acta Mater. · 2007 · 55 · 90710.1016/j.actamat.2006.09.012 ↗
7. Xu · Acta Mater. · 2005 · 53 · 185710.1016/j.actamat.2004.12.036 ↗
8. Kinaka · Mater. Sci. Eng., A · 2008 · 494 · 29910.1016/j.msea.2008.04.039 ↗
9. Ren · J. Alloys Compd. · 2010 · 493 · L4210.1016/j.jallcom.2009.12.195 ↗
10. Nayeb-Hashemi · 1987
11. Miedema · Calphad · 1977 · 1 · 34110.1016/0364-5916(77)90011-6 ↗
12. Han · Intermetallics · 2012 · 20 · 11510.1016/j.intermet.2011.09.002 ↗
13. Li · Mater. Lett. · 2007 · 61 · 501810.1016/j.matlet.2007.03.102 ↗
14. Ma · J. Mater. Res. · 2005 · 20 · 225210.1557/jmr.2005.0307 ↗
15. Kündig · Acta Mater. · 2004 · 52 · 244110.1016/j.actamat.2004.01.036 ↗
16. Park · Appl. Phys. Lett. · 2004 · 85 · 635310.1063/1.1842360 ↗
17. Mattern · Scr. Mater. · 2005 · 53 · 27110.1016/j.scriptamat.2005.04.018 ↗
18. Park · Scr. Mater. · 2007 · 56 · 19710.1016/j.scriptamat.2006.10.020 ↗
19. Chang · Acta Mater. · 2010 · 58 · 248310.1016/j.actamat.2009.12.034 ↗
20. Zeng · Mater. Sci. Eng., A · 2001 · 301 · 15410.1016/S0921-5093(00)01798-6 ↗
21. Kim · Mater. Sci. Eng., A · 2006 · 437 · 24810.1016/j.msea.2006.07.141 ↗
22. Mattern · J. Alloys Compd. · 2011 · 509S · S2310.1016/j.jallcom.2010.10.062 ↗
23. Zheng · Scr. Mater. · 2007 · 56 · 16110.1016/j.scriptamat.2006.09.023 ↗
24. Park · Mater. Trans. · 2004 · 45 · 247410.2320/matertrans.45.2474 ↗
25. Yuan · J. Alloys Compd. · 2005 · 387 · 13410.1016/j.jallcom.2004.06.022 ↗
26. Wright · Mater. Trans. JIM · 2001 · 42 · 64210.2320/matertrans.42.642 ↗
27. Liu · Metall. Mater. Trans. A · 1998 · 29 · 181110.1007/s11661-998-0004-6 ↗
28. Zhang · Acta Mater. · 2003 · 51 · 116710.1016/S1359-6454(02)00521-9 ↗
29. Wang · J. Appl. Phys. · 2006 · 99 · 09350610.1063/1.2193060 ↗
30. Wang · J. Non-Cryst. Solids · 2005 · 351 · 148110.1016/j.jnoncrysol.2005.03.024 ↗