Study on the strength of titanium doped hollow glass microspheres
Source abstract
Abstract
Abstract The composition, structure and strength of titanium doped hollow glass microspheres (HGMs) were studied. Results showed that the strengths of titanium doped glass spheres were determined by the composition, structure and geometric qualities of glass shells. The Young's modulus of HGMs reduced with the increasing titanium concentrations due to the decreased geometric quality of shells and increased with the increase of the fabrication temperature because of the greater loss of alkali oxides at higher temperature. Even though the calculation on the falling process showed that class B HGM had longer average residence time in furnace than class A HGM and consequently greater loss of alkali oxides in glass, the strength of class B HGM was reduced as a result of the generations of oxygen vacancy and phase separation. The strength of class B HGM was improved by compensating oxygen atom by heat treatment in air.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Glass properties and applications · Laser Material Processing Techniques · High-Temperature Coating Behaviors
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (24)
Show source-provided references
1. Manufacture of D–T filled hollow glass microsphere, laser targets10.1063/1.1134280 ↗
2. The physics basis for ignition using indirect-drive targets on the national ignition facility10.1063/1.1578638 ↗
3. Implosion experiments using glass ablators for direct-drive inertial confinement fusion10.1103/PhysRevLett.104.165002 ↗
4. Hollow glass microsphere by sol-gel technology
5. High-Z doping of glass shells10.13182/FST09-A7427 ↗
6. Preparation and characterization of nano-TiO2 doped polystyrene materials by melt blending for inertial confinement fusion10.1081/MB-120030911 ↗
7. Preparation of soluble, linear titanium-containing copolymers by the free-radical copolymerization of vinyl titanate monomers with styrene10.1002/1097-4628(20001003)78:1<190::AID-APP230>3.0.CO;2-M ↗
8. Magnesium and iron loaded hollow glass microspheres (HGMs) for hydrogen storage10.1016/j.ijhydene.2014.03.062 ↗
9. Effect of Co loading on the hydrogen storage characteristics of hollow glass microspheres (HGMs)10.1016/j.ijhydene.2013.12.055 ↗
10. Facile production of optically active hollow glass microspheres for photo-induced outgassing of stored hydrogen10.1016/j.ijhydene.2011.04.195 ↗
11. Influence of titanium doping on the structure and properties of hollow glass microspheres for inertial confinement fusion10.1016/j.jnoncrysol.2016.01.004 ↗
12. Fabrication of titanium doped hollow glass microsphere for inertial confinement fusion targets by dried gel method
13. Preparation of titanium uniformly doped dried gel by sol–gel method
14. Influence of titanium doping on the shell-forming process and geometric properties of hollow glass microspheres
15. Measurement of mechanism properties of hollow glass microspheres used for ICF experiments
16. Strength of aluminum-containing glass shells10.1116/1.570918 ↗
17. J.H. Campbell, J.Z. Grens, J.F. Poco, Preparation and properties of hollow glass microspheres for use in laser fusion experiments, Lawrence Livermore National Laboratory, Livermore, Calif., Nov. 1983, Report UCRL-53516.10.2172/6185129 ↗
18. Fabrication and characterization of millimeter-sized glass shells for inertial confinement fusion targets10.1016/j.cherd.2013.03.010 ↗
19. Effect of phase-separation on nucleation and growth of magnesium-aluminium-titanate crystals in MgO-Al2O3-SiO2-TiO2 glass10.1016/0022-3093(89)90534-6 ↗
20. Production and characterization of hollow glass microspheres with high diffusivity for hydrogen storage10.1016/j.ijhydene.2011.10.034 ↗
21. Sodium and boron vaporization from a boric oxide and a borosilicate glass melt
22. Vogel · 1971 · 73
23. Choice of glass composition for producing hollow microspheres10.1007/BF00677809 ↗
24. Elastic properties and indentation cracking behavior of Na2O-TiO2-SiO2 glasses10.1016/j.jnoncrysol.2015.09.011 ↗