Structural analysis of xCsCl(1 −x)Ga2S3 glasses

Abstract Sulphide glasses doped with rare-earth ions have been demonstrated to be suitable for photonic applications such as optical amplifiers, up-converters and fiber lasers. The substitution of metal halides into the glass network has been shown to result glasses with desirable properties in terms of quantum efficiency and fiber manufacture [J.R. Hector, J. Wang, D. Brady, M. Kluth, D.W. Hewak, W.S. Brocklesby, D.N. Payne, Journal of Non-Crystalline Solids 239 (1998) 176]. To assist in the understanding of this improvement a structural analysis of glasses with a composition x CsCl(1 − x )Ga 2 S 3 has been undertaken in order to examine the nature of the gallium environment. Information collected by high energy X-ray diffraction and neutron diffraction have been analyzed to permit the identification of the structural units as Ga centered tetrahedra. The interconnection between the tetrahedra was found to be predominantly corner sharing.