Structure and properties of Ge2.5PS glasses

Abstract Ge 2.5 PS x glasses were studied with a combination of Raman spectroscopy, nuclear magnetic resonance, and neutron diffraction. From these experiments the distribution of bonding configurations was determined, and used to explain the compositional dependence of the index of refraction and the glass transition temperature. On reducing the sulfur content of these glasses below the stoichiometric amount, the sulfur deficit is accommodated by the progressive loss of the non-bridging sulfur of SPS 3/2 groups, followed by the conversion of the resultant PS 3/2 groups into species such as P 4 S 3 characterized by P–P bonding. The presence of metal–metal bonds involving germanium, found in samples with the lowest sulfur content, was found to be the most important structural feature in determining the optical response.