Erbium- and chlorine-doped fluorozirconate-based glasses for up-converted fluorescence

Abstract A series of glass ceramics was prepared and the structure–property relationships evaluated. The base composition of the series was comprised of fluorozirconate (FZ) and fluorochlorozirconate (FCZ) glass ceramics. Thermal processing of as-made FCZ-based glass ceramics produced sharp peaks in X-ray diffraction patterns, which was attributed to BaCl2 nanocrystals formed in the material; this was not observed in the FZ glass. Up-conversion fluorescence experiments were carried out for both the FZ and FCZ samples doped with erbium. The fact that an increase in the up-conversion efficiency was not observed indicates that erbium ions were not embedded in the BaCl2 nanocrystals. A comparison is made between this series and a similar series that was doped with neodymium.