Casting vacuum effects on the precipitates and magnetic properties of Fe-based glassy alloys

Abstract The crystalline precipitates and magnetic properties of the Fe 61 Co 9 − x Zr 8 Mo 5 W x B 17 (x = 0 and 2) cylinders prepared under various vacuum conditions were investigated in this paper. The fraction of the crystalline precipitates and liquidus temperature of the samples with tungsten content c W = 0 decease with decreasing vacuum, while they increase in the samples with c W = 2 at.%. For both tungsten contents, with decreasing vacuum, the magnetization at room temperature M start and Curie temperature T h c of the samples decrease gradually, but the increment of magnetization Δ M 800 K at 800 K after heating to 973 K increases and the Curie temperature T c c of the residual amorphous matrix shows a decreasing tendency simultaneously. Meanwhile, with decreasing vacuum, Zr–B compounds tend to precipitate easily out from the melt or to remain undissolved during casting, and eutectic Fe–B compounds tend to be formed easily after heating to 973 K. The existence of Zr–B and Fe–B compounds changes the boron content in the residual melt/matrix and consequently affects the magnetic properties of the samples in the as-quenched state and after heating to 973 K.