Improved method for preparation of anhydrous silica by microwave irradiation with spectroscopic characterization and toxicity assay

Abstract Amorphous anhydrous silica SiO 2 (mw) (99.99%) is successfully synthesized through microwave irradiation technique and time of reaction is reduced up to 1 h. The dehydration phase study of Si–water, Si–OH, Si–O–Si networking, elemental analysis and surface morphology was carried out by FTIR, FTNIR, SEM and EDAX spectroscopic techniques. The broad absorption stretching and bending of Si–OH and H 2 O at 3695.38–2832.96 cm − 1 , 1638 cm − 1 and 1191.20–1017.14 cm − 1 completely disappeared and appearance of new bands at 946.93 and 797.63 cm − 1 confirmed the amorphous anhydrous silica with Si–O–Si networking. The SEM images of SiO 2 (mwc) described the smooth and fine particle texture and confirmed 99.99% Si–O–Si networking of anhydrous silica. The 99.99% purity was verified by EDAX spectra which exhibited sharp signals only for oxygen and silicon. Toxicity against Monomorium minimum and Tribolium castaneum with 100% mortality and LT 50 91 min and 7.5 h respectively is being reported. It can be used for long storage of grains in the future.