Structure and properties of Ni60(Nb100−Ta )34Sn6 bulk metallic glass alloys

Abstract Refractory bulk metallic glasses and bulk metallic glass composites are formed in quaternary Ni–Nb–Ta–Sn alloy system. Alloys of composition Ni60(Nb100−xTax)34Sn6 (x = 20, 40, 60, 80) alloys were prepared by injection-casting the molten alloys into copper molds. Glassy alloys are formed in the thickness of half mm strips. With thicker strips (e.g., 1 mm), Nb2O5 and Ni3Sn phases and the amorphous phase form an in situ composite. Glass transition temperatures, crystallization temperatures, and ΔTx, defined as Tx1 − Tg (Tx1: first crystallization temperature, Tg: glass transition temperature) of the alloys increase dramatically with increasing Ta contents. These refractory bulk amorphous alloys exhibit high Young’s modulus (155–170 GPa), shear modulus (56–63 GPa), and estimated yield strength (3–3.6 GPa).