Crystallization of iron phosphate glasses containing up to 19 wt.% UO2.67

Six new glasses having 45-65wt.% P 2 O 5 , 18-42% Fe 2 O 3 , 6.2-18.7%UO 2 . 67 and about 6% (Na 2 O+ Al 2 O 3 + MgO) were finally obtained after melting the batches in Al 2 O 3 /MgO crucibles. The higher Tg-T SOFT values were obtained for glasses AR6 (main components: 57.3%P 2 O 5 . 18.4%Fe 2 O 3. 18-9%UO 2 . 67 ) and AR7 (mc: 65%P 2 O 5 , 19%Fe 2 O3, 9.5%UO 2 . 67 ) and were the most stable glasses against crystallization. The lowest thermal expansion of was measured for AR1 (mc: 54%P 2 O 5 , 27%Fe 2 O 3 , 13.5%UO 2.67 ). AR7 was the least chemically durable composition, whereas the most durable glasses were those containing the highest percentages of UO 2 . 67 (AR6, AR1 and AR5). The least stable glasses against crystallization were AR4 (mc: 45.8% P 2 O 5 , 42.2%Fe 2 O 3 , 6.4%UO 2.67 ), AR5 ( mc: 46.2%P 2 O 5 . 35.4%Fe 2 O 3 . 13.0%UO 2 . 67 ) and AR2 ( mc: 54.2% P 2 O 5 ,33.1 %Fe 2 O 3 . 6.4%UO 2.67 ); their DTA crystallization (Tc) peaks were met at 560 °C (AR4), 600 °C (AR5) and 620 °C (AR2). For these glasses Tc increased with UO 2.67 increasing. The highest internal crystallizations were met for AR2 and AR5. Dendritic crystal growth mode was detected for slowly heat treated (up to 650 °C) AR5 glass. The dendrite arms were clearly seen by SEM and the EBSD (electron back scattered diffraction) patterns (fitted to phase FeP0 4 ) remained unaltered upon moving slightly the detection position throughout those arms.