The residual configurational entropy below the glass transition: Determination for two commercial optical glasses

Ulrich Fotheringham, Andrea Baltes, Rolf Müller, Reinhard Conradt

Journal of Non-Crystalline Solids· Volume 355· Issue 10-12
Publisher page

Abstract

Abstract Essentially from differential scanning calorimetry and viscosimetry, the residual configurational entropy below the glass transition is determined for two linearly cooled commercial optical glasses, K7™ and N-LaK12™ from SCHOTT. The procedure is according to the conventional understanding of glass entropy and the conventional description of the configurational state by a distribution of fictive temperatures. For a cooling rate of 10 K/min, the residual entropy values found below the glass transition are 0.146 J/(g K) for K7™ and 0.148 J/(g K) for N-LaK12™. The result is discussed comparing with both the lower limit for the residual entropy resulting from the reversibly exchanged heat ( ∫ dq / T , ‘Clausius limit’) and the upper limit given by the configurational entropy of an equilibrium liquid with the same fictive temperature. The difference between the residual entropy and its lower limit is equal to the entropy generation due to the fall-out from equilibrium during linear cooling. The difference between the residual entropy and its upper limit is the driving force of the crossover- (or Kovacs-) effect. It turns out that the difference between the residual entropy and the Clausius limit is very small. The values found amount to less than 0.0001 J/(g K) for both glasses. Therefore, this difference can be neglected concerning the extrapolation of the Adam–Gibbs relation to low temperatures.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Material Dynamics and Properties · Phase Equilibria and Thermodynamics · Thermodynamic properties of mixtures

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (35)

Show source-provided references
1. Gutzow · Phys. Chem. Glasses: Eur. J. Glass Sci. Technol. B · 2007 · 48 · 168
2. Mauro · J. Chem. Phys. · 2007 · 126 · 18451110.1063/1.2731774 ↗
3. Gupta · J. Chem. Phys. · 2007 · 126 · 22450410.1063/1.2738471 ↗
4. Narayanaswamy · J. Am. Ceram. Soc. · 1971 · 54 · 49110.1111/j.1151-2916.1971.tb12186.x ↗
5. Mauro · J. Am. Ceram. Soc. · 2009 · 92 · 7510.1111/j.1551-2916.2008.02851.x ↗
6. Langer · Phys. Rev. B · 1990 · 41 · 226110.1103/PhysRevB.41.2261 ↗
7. Moynihan · J. Non-Cryst. Solids · 2000 · 274 · 13110.1016/S0022-3093(00)00198-8 ↗
8. Tool · J. Am. Ceram. Soc. · 1946 · 29 · 24010.1111/j.1151-2916.1946.tb11592.x ↗
9. Moynihan · J. Am. Ceram. Soc. · 1976 · 59 · 1210.1111/j.1151-2916.1976.tb09376.x ↗
10. DeBolt · J. Am. Ceram. Soc. · 1976 · 59 · 1610.1111/j.1151-2916.1976.tb09377.x ↗
11. Adam · J. Chem. Phys. · 1965 · 43 · 13910.1063/1.1696442 ↗
12. Hodge · J. Am. Ceram. Soc. · 2008 · 91 · 76610.1111/j.1551-2916.2007.02127.x ↗
13. Scherer · J. Am. Ceram. Soc. · 1984 · 67 · 50410.1111/j.1151-2916.1984.tb19643.x ↗
14. Bouhifd · Geochim. Cosmochim. Acta · 1999 · 63 · 242910.1016/S0016-7037(99)00145-3 ↗
15. Prigogine · 1954
16. Richet · Geochim. Cosmochim. Acta · 1984 · 48 · 45310.1016/0016-7037(84)90274-6 ↗
17. Scherer · 1992
18. Nemilov · 1995
19. Inaba · J. Non-Cryst. Solids · 2003 · 325 · 25810.1016/S0022-3093(03)00315-6 ↗
20. Burns · 1985
21. Nemilov · 1995
22. Jäckle · Philos. Mag. B · 1981 · 44 · 53310.1080/01418638108224037 ↗
23. Primenko · Glass Ceram. · 1978 · 35 · 66610.1007/BF00696600 ↗
24. Bottinga · Chem. Geol. · 1996 · 128 · 12910.1016/0009-2541(95)00168-9 ↗
25. Nieuwenhuizen · Phys. Rev. Lett. · 1998 · 80 · 558010.1103/PhysRevLett.80.5580 ↗
26. DeHoff · 2006
27. de Groot · 1984
28. Garden · J. Chem. Phys. · 2008 · 129 · 4450810.1063/1.2958913 ↗
29. de Groot · 1984
30. Bottinga · Chem. Geol. · 1996 · 128 · 12910.1016/0009-2541(95)00168-9 ↗
31. Höhne · 1996
32. Fotheringham · Thermochim. Acta · 2007 · 461 · 7210.1016/j.tca.2007.06.007 ↗
33. Fotheringham · 1998
34. Technical Information TIE-37, Schott AG, Business Segment Advanced Optics, Mainz, Germany, August 2006.
35. ASTM C623-92, Standard test method for Young’s modulus, shear modulus, and Poisson’s ratio for glass and glass ceramics by resonance method, re-approved 2000.