Sol–gel preparation and optical properties of SiO2–Ta2O5 glass

Abstract Tantalum-doped silica glass was fabricated by the sol–gel process in order to obtain a glass with a high refractive index for optical use. A crack-free, clear glass rod was successfully prepared from a low-density gel and used as the core material for fabricating optical fibers. Transmission loss in the fabricated fibers was high, in the range of 10 3 –10 4 dB/km, which may be caused by coloration due to the multivalency of tantalum; however, the loss was reduced by nearly one order of magnitude by heat treatment at 800 °C, that is, to 75 dB/km at a wavelength of 0.8 μm.