Texture and nanostructure of chromia aerogels prepared by urea-assisted homogeneous precipitation and low-temperature supercritical drying

Abstract Mesoporous chromia aerogels with a surface area of 484–735 m 2 g −1 , a pore volume of 0.4–0.9 cm 3 g −1 and a pore diameter of 3–9 nm were prepared by urea-assisted homogeneous precipitation from an aqueous Cr(NO 3 ) 3 solution, followed by continuous supercritical extraction with CO 2 under different conditions (pressure and time) after replacement of the water with a hexane/2-butanol mixture. The texture and chemistry of the aerogels transformed by heating in air or an inert atmosphere and the structure of the nanoparticles were characterized by means of N 2 -adsorption isotherms, AA, HRTEM, FTIR, a variety of thermoanalytical methods (TPD, DSC, TGA, TPO–TPK) and X-ray diffraction in combination with structure modeling. At the CO 2 extraction stage, a pressure of about 400 bars was critical for production of aerogels with surface areas >700 m 2 g −1 . The fresh chromia aerogels consisted of closely packed almost globular, 3- to 5-nm nanoparticles with a structure analogous to that of monoclinic α-CrOOH, in which half of the O atoms and OH groups were replaced with coordinately bonded water molecules. After dehydration at 550–600 K, the materials retained their texture, being converted to faceted 3- to 5-nm nanoparticles, consisting of two-dimensional fragments (clusters) of α-CrOOH crystals built on [Cr(OH) 3 O 3 ] octahedra without bonding along the Z -axis. The texture of dehydrated chromia aerogels was stable at temperatures up to 650 K in air and up to 773 K in an inert atmosphere. At higher temperatures, the material underwent a glow transition, yielding microcrystalline 50-nm particles with the well-defined structure of α-Cr 2 O 3 and a surface area 2 g −1 .